养护条件对UHPC强度和毛细吸水性的影响
PDF下载 (339)施范铧,贺智敏,刘 畅,魏玲玲,巴明芳.养护条件对UHPC强度和毛细吸水性的影响[J].宁波大学学报(理工版),2022,35(3):10-18.DOI:
SHI Fanhua,HE Zhimin,LIU Chang,WEI Lingling,BA Mingfang.Effect of curing condition on mechanical strength and capillary water absorption of UHPC[J].Journal of Ningbo University(Natural Science & Engineering Edition),2022,35(3):10-18.DOI:
| Title: | Effect of curing condition on mechanical strength and capillary water absorption of UHPC |
| 作者: | 施范铧, 贺智敏, 刘 畅, 魏玲玲, 巴明芳 |
| Author(s): | SHI Fanhua, HE Zhimin, LIU Chang, WEI Lingling, BA Mingfang |
| 关键词: | 超高性能混凝土; 养护条件; 毛细吸水性; 孔结构; 力学强度 |
| Keywords: | ultra-high performance concrete; curing condition; capillary water absorption; pore structure; mechanical strength |
| 分类号: | TU528 |
| 文献标识码: | A |
| 摘要: | 为优化超高性能混凝土(UHPC)预制构件养护工艺, 研究了不同养护条件对UHPC强度和毛细吸水性的影响, 并采用孔结构测试、热重分析和扫描电镜观察, 对其机理进行了分析. 结果表明 热养护显著提高了UHPC的7d强度, 这与加速火山灰反应有关, 但高温和干热养护对其后期强度增大不利, 甚至出现约3％的强度倒缩; 不论何种养护, UHPC总体均具有较低的毛细吸水性, 毛细吸水系数随试件吸水时间和养护龄期增长而显著降低, 干热养护试件的毛细吸水性高于其他养护条件; 从综合性能考虑, 干热养护温度宜控制在100℃以下, 超过150℃会显著增大UHPC的总孔和大孔孔隙率, 并增大毛细吸水性. 电镜观察到热养护试件内部存有微裂纹, 而钢纤维可以抑制周围水化产物微裂纹的发生. |
| Abstract: | In order to optimize the curing process of ultra-high performance concrete (UHPC) prefabricated components, the effect of different curing conditions on mechanical strength and capillary water absorption of UHPC was investigated, and the mechanism was analyzed by pore structure test, thermogravimetric analysis and scanning electron microscope. Test results indicate that, heat curing regime has a very significant increase on 7 day mechanical strength, which is most likely related to acceleration of the pozzolanic reaction. However, the high temperature curing and dry-heat curing hinder its later strength growth, with its 28 day strength is even lower than 7 day strength. UHPC generally has lower capillary water absorption. The capillary water absorption coefficient drops remarkably with the extension of specimen suction time and curing age. The capillary water absorption of dry heat curing specimen is higher than those of other curing condition. Considering the comprehensive performance, the dry heat curing temperature should be controlled below 100℃. When the hot curing temperature is over 150℃, total and large pore porosity of UHPC will increase significantly, and the capillary water absorption will also increase. It was observed by scanning electron microscope that a few micro cracks appearal in the heat curing specimen, but steel fiber could restrain the micro cracks around the hydration products. |
| 参考文献 /References: | [1] Shi C J, Wu Z M, Xiao J F, et al. A review on ultra high performance concrete: Part I. Raw materials and mixture design[J]. Construction and Building Materials, 2015, 101:741-751. [2] 孙瑜, 王焕然, 王飞, 等. 波形钢板-UHPC组合桥面板结构截面优化[J]. 宁波大学学报(理工版), 2020, 33(3): 105-110. [3] 赵金侠, 黄亮, 谢建和. 不同配比和养护条件对超高性能混凝土微观结构的影响[J]. 中国公路学报, 2019, 32(7):111-119. [4] Liu J T, Yang Y, Gu C P, et al. Influence of dry heating regime on the mechanical and shrinkage properties of reactive powder concrete[J]. Journal of Zhejiang University: Science A, 2018, 19(12):926-938. [5] Yang S L, Millard S G, Soutsos M N, et al. Influence of aggregate and curing regime on the mechanical properties of ultra-high performance fibre reinforced concrete (UHPFRC)[J]. Construction and Building Materials, 2009, 23(6):2291-2298. [6] Hiremath P N, Yaragal S C. Effect of different curing regimes and durations on early strength development of reactive powder concrete[J]. Construction and Building Materials, 2017, 154:72-87. [7] 牛旭婧, 乜颖, 朋改非, 等. 养护制度对超高性能混凝土抗高温爆裂性能的影响[J]. 硅酸盐学报, 2020, 48(8): 1212-1222. [8] Shen P L, Lu L N, He Y J, et al. The effect of curing regimes on the mechanical properties, nano-mechanical properties and microstructure of ultra-high performance concrete[J]. Cement and Concrete Research, 2019, 118: 1-13. [9] Wang X B, Sun M J, Guo S B. Water absorption characteristics of cement-based materials based on the chemical reaction[J]. Construction and Building Materials, 2019, 220:607-614. [10] Zhang P, Wittmann F H, Vogel M, et al. Influence of freeze-thaw cycles on capillary absorption and chloride penetration into concrete[J]. Cement and Concrete Research, 2017, 100:60-67. [11] Wang Y R, Cao Y B, Zhang P, et al. Water absorption and chloride diffusivity of concrete under the coupling effect of uniaxial compressive load and freeze-thaw cycles[J]. Construction and Building Materials, 2019, 209:566-576. [12] GB/T 17671-1999. 水泥胶砂强度检测方法[S]. [13] Martys N S, Ferraris C F. Capillary transport in mortars and concrete[J]. Cement and Concrete Research, 1997, 27(5):747-760. [14] Ngala V T, Page C L. Effects of carbonation on pore structure and diffusional properties of hydrated cement pastes[J]. Cement and Concrete Research, 1997, 27(7): 995-1007. [15] Helmi M, Hall M R, Stevens L A, et al. Effects of high-pressure/temperature curing on reactive powder concrete microstructure formation[J]. Construction and Building Materials, 2016, 105:554-562. [16] 鲍玖文, 胡文文, 张鹏, 等. 有机硅憎水剂对混凝土强度与毛细吸水性能的影响[J]. 硅酸盐学报, 2020, 48(10):1644-1652. |
| 备注/Memo: | 收稿日期:2021-11-26.宁波大学学报（理工版）网址:http://journallg.nbu.edu.cn/ 基金项目:浙江省自然科学基金（LY17E080007）;宁波市自然科学基金（202003N4137）;宁波大学滨海城市轨道交通协同创新中心开放基金（2020004）. 第一作者:施范铧（1997－）,男,浙江永康人,在读硕士研究生,主要研究方向:混凝土材料.E-mail:2318878173@qq.com *通信作者:贺智敏（1973－）,男,湖南邵阳人,博士/副教授,主要研究方向:混凝土材料.E-mail:hezhimin@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |