基于咔唑结构的共轭聚合物太阳能电池材料的合成及表征
PDF下载 (569)缴春明 1,徐 清 1*,周刚明 2.基于咔唑结构的共轭聚合物太阳能电池材料的合成及表征[J].宁波大学学报(理工版),2016,29(2):128-132.DOI:
JIAO Chun-ming 1,XU Qing 1*,ZHOU Gang-ming 2.Synthesis and Characterization of Carbazole Based Conjugated Polymer for Organic Photovoltaics[J].Journal of Ningbo University(Natural Science & Engineering Edition),2016,29(2):128-132.DOI:
| Title: | Synthesis and Characterization of Carbazole Based Conjugated Polymer for Organic Photovoltaics |
| 作者: | 缴春明 1, 徐 清 1*, 周刚明 2 |
| Author(s): | JIAO Chun-ming 1, XU Qing 1*, ZHOU Gang-ming 2 |
| 关键词: | 烷基化咔唑; 氟代苯并噻二唑; 共轭聚合物; 聚合物太阳能电池 |
| Keywords: | alkylcarbazole; fluorined benzothiadiazole; conjugated polymers; polymer solar cells |
| 分类号: | O635 |
| 文献标识码: | A |
| 摘要: | 通过Sukuzi偶联反应, 分别以3种烷基(正辛基、异辛基和十二烷基)咔唑为给体单元, 4,7-二(5-溴-3-己基噻吩-2-基)-5,6-二氟-[2,1,3]苯并噻二唑为受体单元, 合成了一系列共轭聚合物, 并研究了不同烷基链对聚合物光吸收性能和电化学能级的影响. 结果表明: 相比于支化的异辛基和较长碳链的十二烷基取代的聚合物, 正辛基取代的聚合物有更广的吸收范围和较窄的光学带隙, 通过XRD可知π-π堆积的间距为4.13 ?; 通过理论计算, 其开路电压(VOC)可达1.15 V, 更适合用作聚合物太阳能电池材料. |
| Abstract: | A series of conjugated polymers are synthesized successfully from donor unit with three kinds of alkyls (-octyl, -isooctyl, -dodecyl) carbazole and acceptor unit based on 4,7-bis(5-bromo-3-hexylthiophen-2- yl)-5,6-difluoro-[2,1,3]benzothiadiazole via Suzuki coupling reaction. The influence of optical absorption properties and electrochemical energy levels from different kinds of alkyl chains is investigated. Compared with the copolymers of branching isooctyl chain and dodecyl possessing longer carbon chains, the copolymer replaced with octyl exhibits a wider absorption region and narrower optical band gap. Besides, the spacing of π-π stacking is found to be 4.13 ? via XRD spectra, open circuit voltage calculated by the theoretical formula reaches 1.15 V, which proves to be the suitable material for manufacturing the polymer solar cells. |
| 参考文献 /References: | [1] LI G, ZHU R, YANG Y. Polymer solar cells[J]. Nat Photonics, 2012, 6(3):153-161. [2] LI W W, FURLAN A, HENDRIKS K H, et al. Efficient tandem and triple-junction polymer solar cells[J]. J Am Chem Soc, 2013, 135(15):5529-5532. [3] KREBS F C, FYENBO J, TANENBAUM D M, et al. The OE-A OPV demonstrate anno domini 2011[J]. Energy Environ Sci, 2011, 4(10):4116-4123. [4] KREBS F C, GEVORGYAN S A, ALSTRUP J A. Roll-to-roll process to flexible polymer solar cells: Model studies, manufacture and operational stability studies[J]. J Mater Chem, 2009, 19(30):5442-5451. [5] PARK S H, ROY A, BEAUPR? S, et al. Bulk hetero- junction solar cells with internal quantum efficiency approaching 100%[J]. Nat Photonics, 2009, 3(5):297-302. [6] LIU Q, LI C H, JIN E Q, et al. 9-Arylidene-9H- Fluorene-containing polymers for high efficiency poly- mer solar cells[J]. ACS Appl Mater Interfaces, 2014, 6(3): 1601-1607. [7] HE Z C, ZHONG C M, SU S J, et al. Enhanced power- convension efficiency in polymer solar cells using an inverted device structure[J]. Nat Photonics, 2012, 6(9): 591-595. [8] KIM J H, SONG C E, KIM B S, et al. Thieno[3,2-b] thiophene-substituted benzo[1,2-b:4,5-b’]dithiophene as a promising building block for low bandgap semi- conducting polymers for high-performance single and tandem organic photovoltaic cells[J]. Chem Mater, 2014, 26(2):1234-1242. [9] DENNLER G, SCHARBER M C, BRABEC C J. Polymer-fullerene bulk-heterojunction solar cells[J]. Adv. Mater., 2009, 21(13):1323-1338. [10] ZHOU H X, YANG L Q, STUART A C, et al. Develop- ment of fluorinated benzothiadiazole as a structural unit for a polymer solar cell of 7% efficiency[J]. Angew Chem, 2011, 123(13):3051-3054. [11] STUART A C, TUMBLESTON J R, ZHOU H X. et al. Fluorine substituents reduce charge recombination and drive structure and morphology development in polymer solar cells[J]. J Am Chem Soc, 2013, 135(5):1806-1815. [12] BLOUIN N, MICHAUD A, LECLERC M. A low- bandgap poly(2,7-carbazole) derivative for use in high- performance solar cells[J]. Adv Mater, 2007, 19(17): 2295-2300. [13] JIN E Q, DU C, WANG M, et al. Dibenzothio- phene-based planar conjugated polymers for high effi- ciency polymer solar cells[J]. Macromolecules, 2012, 45 (19):7843-7854. [14] SCHARBER M C, M?HLBACHER D, KOPPE M, et al. Design rules for donors in bulk-heterojunction solar cells-towards 10% energy-conversion efficiency[J]. Adv Mater, 2006, 18(6):789-794. [15] KIM J H, KIM H U, KANG I N, et al. Incorporation of pyrene unites to improve hole mobility in conjugated polymers of organic solar cells[J]. Macromolecules, 2012, 45(21):8628-8638. [16] SUN J M, ZHU Y X, XU X F, et al. High efficiency and high VOC inverted polymer solar cells based on a low- lying HOMO polycarbazole donor and a hydrophilic polycarbazole interlayer on ITO cathode[J]. J Phys Chem C, 2012, 116(27):14188-14198. |
| 备注/Memo: | 收稿日期: 2014－10－08. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/基金项目: 浙江省自然科学基金（LY12B04001）; 浙江省科技厅创新团队自主设计项目（2011R50001-08）; 宁波市自然科学基金（2014A610045）; 宁波市江北区科技计划项目（2013A0125）; 刘孔爱菊教育基金.第一作者: 缴春明（1988－）, 男, 河北廊坊人, 在读硕士研究生, 主要研究方向: 有机光电功能材料. E-mail: jld670541cmgf@163.com*通信作者: 徐清（1976－）, 男, 湖北武汉人, 博士/副教授, 主要研究方向: 有机聚合物光电功能材料. E-mail: xuqing@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |