PDF下载 (777)闫加利,柳俊哲 *,蒋 义,戴燕华,耿俊迪,姚森元.亚硝酸根浓差作用下混凝土中钢筋的腐蚀特征[J].宁波大学学报(理工版),2017,30(2):95-99.DOI:
YAN Jia-li,LIU Jun-zhe *,JIANG Yi,DAI Yan-hua,GENG Jun-di,YAO Sen-yuan.Corrosion characterization of the steel bar in reinforced concrete under differential nitrite ion concentration[J].Journal of Ningbo University(Natural Science & Engineering Edition),2017,30(2):95-99.DOI:
| Title: | Corrosion characterization of the steel bar in reinforced concrete under differential nitrite ion concentration |
| 作者: | 闫加利, 柳俊哲 *, 蒋 义, 戴燕华, 耿俊迪, 姚森元 |
| Author(s): | YAN Jia-li, LIU Jun-zhe *, JIANG Yi, DAI Yan-hua, GENG Jun-di, YAO Sen-yuan |
| 关键词: | 钢筋混凝土; 亚硝酸盐; 浓差; 钢筋腐蚀 |
| Keywords: | reinforced concrete; nitrite; concentration difference; steel corrosion |
| 分类号: | TU528.0 |
| 文献标识码: | A |
| 摘要: | 通过含氯盐与亚硝酸盐钢筋混凝土加速腐蚀试验, 结合腐蚀面积率和失重率综合评价亚硝酸盐掺量均匀以及两侧存在浓差时钢筋的腐蚀情况. 结果表明: 亚硝酸盐掺量均匀时, 随着 浓度增加阻锈效果增强, 且n /n 比值达到1.2时完全阻锈; 亚硝酸盐存在浓度差时, 即使n /n 为1.5也不能完全阻锈; 大阳极 浓度变化不会影响阻锈性能, 但小阳极上 浓度变化引起的浓差对阻锈性能有影响, 甚至加速腐蚀; 钢筋两侧 浓度差保持不变时, 改变阴、阳两极面积比对钢筋的腐蚀影响较小; 高浓度的 作用时, 钢筋两侧的 浓度差增大, 导致钢筋加速腐蚀. |
| Abstract: | In accelerated steel corrosion experiment of reinforced concrete containing various quantities of calcium chloride and calcium nitrite, the corrosion characterization of steel under uniform and differential nitrite ion concentration was determined by mass loss degree and corrosion area ratio. The results showed that the effect of corrosion prevention enhanced with the increase of nitrite, and the corrosion was inhibited nearly completely at a molar ratio of 1.2 or more in the concrete with uniform molar ratios. However, the corrosion was not inhibited completely at a molar ratio of 1.5 when the nitrite was different. Unlike the anode, however, the content changes of nitrite in cathode sometimes even weaken the anti-corrosion effect of steel. Moreover, the cathode and anode area ratio did not cause much difference about anti-corrosion effect by keeping the nitrite constant. While under high concentration of nitrite, the bipolar nitrite concentration difference turned out to be speeding up the corrosion of the steel. |
| 参考文献 /References: | [1] SANCHEZ M, ALONSO M C. Electrochemical chloride removal in reinforced concrete structures: Improvement of effectiveness by simultaneous migration of calcium nitrite[J]. Construction and Building Materials, 2011, 25 (2):873-878. [2] ZHANG Z W, LI Y S, LIU R. An analytical model of stresses in adhesive bonded interface between steel and bamboo plywood[J]. International Journal of Solids and Structures, 2015, 52:103-113 [3] LI Y S, SHEN H Y, SHAN W, et al. Flexural behavior of lightweight bamboo-steel composite slabs[J]. Thin-walled Structures, 2012, 53:83-90. [4] TANG Y M, ZHANG G D, ZUO Y. The inhibition effects of several inhibitors on rebar in acidified concrete pore solution[J]. Construction and Building Materials, 2012, 28(1):327-332. [5] KR?LIKOWSKIA A, KUZIAKB J. Impedance study on calcium nitrite as a penetrating corrosion inhibitor for steel in concrete[J]. Electrochimica Acta, 2011, 56(23): 7845-7853. [6] 柳俊哲, 邢锋, 贺智敏, 等. 钢筋混凝土中亚硝酸根与氯离子的临界摩尔比[J]. 硅酸盐学报, 2010, 38(4):615- 620. [7] 刘志勇, 缪昌文, 孙伟. 迁移性阻锈剂对氯盐污染钢筋混凝土耐久性的影响(II): 长期效果、形貌与机理分析[J]. 硅酸盐学报, 2010, 38(7):1323-1327. [8] 李遵云, 杨林, 屠柳青. 新型迁移型钢筋阻锈剂对混凝土耐久性能的影响[J]. 新型建筑材料, 2014, 41(3):9-15. [9] PRITZL M D, TABATABAI H, GHORBANPOOR A. Long term chloride profiles in bridge decks treated with penetrating sealer or corrosion inhibitors[J]. Construction and Building Materials, 2015, 101:1037-1043. [10] 李翔, 韩飞, 吕晓霞, 等. 阻锈剂与矿物掺合料对锈蚀混凝土修复砂浆的性能影响[J]. 混凝土与水泥制品, 2014(9):15-19. [11] 日本コンクリート工学協会. コンクリート構造物の腐食防食に関する試験方法ならびに規準(案)[S]. 1997:7-9. [12] 柳俊哲, 冯奇, 李玉顺. 亚硝酸盐在混凝土中的阻锈效果[J]. 硅酸盐学报, 2004, 32(7):854-857. |
| 备注/Memo: | 收稿日期: 2016－06－02. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 国家自然科学基金（51478227）; 宁波大学研究生科研创新基金资助项目（G15058）. 第一作者: 闫加利（1993－）, 女, 安徽金寨人, 在读硕士研究生, 主要研究方向: 混凝土耐久性. E-mail: 963122649@qq.com *通信作者: 柳俊哲（1964－）, 男, 黑龙江五常人, 博导/教授, 主要研究方向: 混凝土耐久性. E-mail: junzheliu@163.com 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |