复合型阻锈剂阻锈性能及机理研究
PDF下载 (485)邢祥伟,柳俊哲*,姚森元,杨梦娜.复合型阻锈剂阻锈性能及机理研究[J].宁波大学学报(理工版),2019,32(3):80-86.DOI:
XING Xiang-wei,LIU Jun-zhe*,YAO Sen-yuan,YANG Meng-na.Corrosion resistance and mechanism of composite corrosion inhibitor[J].Journal of Ningbo University(Natural Science & Engineering Edition),2019,32(3):80-86.DOI:
| Title: | Corrosion resistance and mechanism of composite corrosion inhibitor |
| 作者: | 邢祥伟, 柳俊哲*, 姚森元, 杨梦娜 |
| Author(s): | XING Xiang-wei, LIU Jun-zhe*, YAO Sen-yuan, YANG Meng-na |
| 关键词: | 复合阻锈剂 ; 亚硝酸盐; 磷酸氢二钠; 阻锈机理 |
| Keywords: | composite corrosion inhibitor; nitrite; dibasic sodium phosphate; corrosion-resistant mechanism |
| 分类号: | TU528.0 |
| 文献标识码: | A |
| 摘要: | 基于阴阳两极阻锈剂阻锈机理, 通过盐水浸渍和钢筋混凝土阻锈试验, 得到阻锈效果良好的复合型阻锈剂, 并通过X射线衍射技术(XRD)和电镜扫描分析技术(SEM)微观手段探讨了其作用机理. 结果表明: 阻锈剂单掺时, 阳极型阻锈剂比阴极型阻锈剂具有更好的阻锈效果, 阴阳两极阻锈剂复合掺加后可得到优于单掺的阻锈效果; 磷酸盐的掺入能更好地改善亚硝酸盐在低掺量时引起的点蚀效应; 磷酸氢二钠与亚硝酸钠以1:1的质量配比时, 阻锈效果最好, 且混凝土的密实性得到提高. |
| Abstract: | By both the salt-water impregnation test and the corrosion resistance test of reinforced concrete, a composite corrosion inhibitor with good performance was obtained based on the corrosion inhibiting mechanisms of anodic and cathodic corrosion inhibitors. Results indicated that when the corrosion inhibitor was single-doped, the rust-inhibiting effect in cathodic corrosion inhibitors was weaker than that of the anode corrosion inhibitors. Moreover, composite corrosion inhibitor had better rust resistance than single component corrosion inhibitor. The addition of phosphate could improve the pitting effect of nitrite at low concentration. The new composite corrosion inhibitor had great inhibiting and synergistic effect, and could improve the compactness of concrete when the mass ratio of disodium hydrogen phosphate to sodium nitrite is 1:1. |
| 参考文献 /References: | [1].仲朝明, 邵正明, 高汉青, 等. 亚硝酸盐类钢筋阻锈剂应用技术问题探讨[J]. 混凝土, 2009(12):4651. [2].马世豪, 李伟华, 郑海兵, 等. 钢筋阻锈剂的阻锈机理及性能评价的研究进展[J]. 腐蚀与防护, 2017, 38(12): 963968. [3].Okeniyi J O, Omotosho O A, Ajayi O O, et al. Effect of potassium-chromate and sodium-nitrite on concrete steel- rebar degradation in sulphate and saline media[J]. Construction and Building Materials, 2014, 50:448-456. [4].Zhang Z W, Li Y S, Liu R. Failure behavior of adhesive bonded interface between steel and bamboo plywood[J]. Journal of Adhesion Science and Technology, 2016, 30 (19):2081-2099. [5].Valcarce M B, Vázquez M. Carbon steel passivity examined in solutions with a low degree of carbonation: The effect of chloride and nitrite ions[J]. Materials Chemistry and Physics, 2009, 115:313-321. [6].唐聿明, 牛, 林冰, 等. NO2-及其浓度对混凝土模拟孔隙液中碳钢早期孔蚀的作用[J]. 腐蚀科学与防护技术, 2015, 27(2):123128. [7].陈明实, 孙丛涛, 于景飞. 钢筋阻锈剂在混凝土中的阻锈机理[J]. 混凝土, 2015(6):8083. [8].柳俊哲, 孙武, 贺智敏, 等. 亚硝酸盐在混凝土结构中的阻锈作用英文[J]. 硅酸盐学报, 2014, 42(5):607612. [9].杜荣归, 胡融刚, 胡仁, 等若干无机缓蚀剂对混凝土中钢筋的阻锈作用[J]厦门大学学报自然科学版, 2001, 40(4):908-913. [10].Blustein G, Rodringuze J, Romanogli R, et al. Inhibition of steel corrosion by calcium benzoate adsorption in nitrate solutions[J]. Corrosion Science, 2005, 47(2):369- 383. [11].Ashassi S H, Asghari E. Effect of soulution hydrody- namics on corrosion inhibition performance of zinc solfate in neutral solution[J]. Journal of the Electroche- mical Society, 2011, 159(1):C1-C7. [12].杜荣归, 王周成, 黄若双, 等. LD-2复合缓蚀剂对海水介质混凝土中钢筋阻锈作用研究[J]. 电化学, 2001, 7(4): 494-500. [13].Boucherit M, Amzert S A, Arbaoui F, et al. Pitting corrosion in presence of inhibitors and oxidants[J]. Anti-Corrosion Methods and Materials, 2008, 55(3):115- 122. [14].吕明敏. 钢筋阻锈剂的种类与发展现状分析[J]. 桥隧工程, 2018,2):204-206. [15].Tang Y B, Wang S N, Xu Y P. Influence of calcium nitrite on passive films of rebar in simulated concrete pore solution[J]. Materials Protection, 2017, 50(8):28-31. [16].Shi J J, Sun W. Effect of phosphate on the chloride- induced corrosion behavior of reinforcing steel in mortars [J]. Cement and Concrete Composites, 2014, 45:166-175. [17].Etteyeb N, Dhouibi L, Takenouti H. Protection of reinforcement steel corrosion by phenylphos-phonic acid pre-treatment, part II: Tests in mortar medium[J]. Cement and Concrete Composites. 2016, 65(3):94-100. [18].Zhang Z W, Li Y S, Liu R. An analytical model of stresses in adhesive bonded interface between steel and bamboo plywood[J]. International Journal of Solids and Structures, 2015, 52:103-113. [19].Verbruggen H, Terryn H, Graeve I D. Inhibitor evaluation in different simulated concrete pore solution for the protection of steel rebars[J]. Construction and Building Materials, 2016, 124:887-896. [20].张大全, 安仲勋, 潘庆谊, 等. 吗啉多胺对混凝土钢筋的阻锈作用[J]. 材料保护, 2004,8):4-6. [21].Nami C K. Multi-functional organic corrosion inhibitor[J]. Cement and Concrete Composites, 2004, 26(3):199-207. [22].加利柳俊哲蒋义等0(2):95-99. [23].戴燕华, 柳俊哲, 蒋义, 等. 基于亚硝酸盐的复合型阻锈剂性能研究[J]. 宁波大学学报(理工版), 2016, 29(4): 96-100. [24].Shi W, Wang T Z, Dong Z H, et al. Application of wire beam electrode technique to investigate the migrating behavior of corrosion inhibitors in mortar[J]. Construction and Building Materials, 2017, 134:167-175. [25].Bastidas D M, Criado M, Lglesia V M L, et al. Comparative study of three sodium phosphates as corrosion inhibitors for steel reinforcements[J]. Cement and Concrete Composites, 2013, 43:31-38. |