高抗折硫氧镁基无机复合胶凝材料的制备及其机理
PDF下载 (17398)朱杰兆,薛 涛,巴明芳*.高抗折硫氧镁基无机复合胶凝材料的制备及其机理[J].宁波大学学报(理工版),2017,30(6):66-72.DOI:
ZHU Jie-zhao,XUE Tao,BA Ming-fang*.Preparation and mechanism of magnesium oxysulfate based inorganic cementitious material with high flexural strength[J].Journal of Ningbo University(Natural Science & Engineering Edition),2017,30(6):66-72.DOI:
| Title: | Preparation and mechanism of magnesium oxysulfate based inorganic cementitious material with high flexural strength |
| 作者: | 朱杰兆, 薛 涛, 巴明芳* |
| Author(s): | ZHU Jie-zhao, XUE Tao, BA Ming-fang* |
| 关键词: | 柠檬酸改性; 硫氧镁胶凝材料; 硅灰; 高抗折 |
| Keywords: | citric acid modification; magnesium oxysulfate; silica fume; high flexural strength |
| 分类号: | TQ52 |
| 文献标识码: | A |
| 摘要: | 为了制备具有高抗折性能的硫氧镁基胶凝材料, 分别研究了不同掺量硅灰取代轻烧氧化镁粉对柠檬酸改性硫氧镁(CMOS)胶凝材料性能的影响及机理. 结果表明: 掺加硅灰之后, 制备的柠檬酸改性硫氧镁胶凝材料抗折抗压强度均得到了提高. 当硅灰取代掺量在5%~10%质量分数时, 柠檬酸改性硫氧镁胶凝材料各个龄期的力学性能最优, 其中, 28d抗折强度达到了22~23 MPa左右, 这比相同水灰比条件下普通硅酸盐水泥P.O42.5的抗折强度提高了238%. 研究还发现, 硅灰取代掺量在5%~10%质量分数范围时, 所制备的硫氧镁基胶凝材料的耐水系数达到了0.85以上, 表明该高抗折硫氧镁基胶凝材料具有较高的耐水性, 完全适用于受水浸泡或处于潮湿环境的重要结构中. |
| Abstract: | In order to prepare magnesium oxysulfate cementitious material with high flexural properties, the effects of different amount of silica fume instead of light burned magnesia powder on citri-acid-modified magnesium oxysulfate (CMOs) cementitious materials were investigated. The results show that the compressive strength of CMOs materials is improved by adding silica fume. When the dosage of silica fume is 5%-10%, the optimum mechanical properties of CMOs cemented materials are obtained at different ages. At age of 28 days, its flexural strength reaches 22-23MPa which increases by 238% comparing with ordinary Portland cement P.O42.5 under the same water cement ratio condition. The results also shows that when replacement content is 5%-10%, the softening coefficient of the prepared CMOs cementing material is more than 0.85, which indicates that prepared CMOs cemented materials has much higher water resistance and it could be adopted in some key structures soaking in water or in wet environment. |
| 参考文献 /References: | [1].URWONGSE L, SORRELL C A. Phase relationships in magnesium oxysulfate cements[J]. Journal of the American Ceramic Society, 1980, 63(9/10):523-526. [2].李颖, 余红发, 董金关, 等. 氯氧镁胶凝材料吸潮返卤泛霜的研究进展[J]. 硅酸盐报, 2010, 29(4):858-865. [3].李早元, 靳东旭, 周超, 等. 镁氧水泥用于油井堵漏及暂闭的室内研究[J]. 西南石油大学学报(自然科学版), 2011, 33(5):152-156. [4].ZHOU X, LI Z. Light-weight wood-magnesium oxychlo- ride cement composite building products made by extrusion[J]. Construction and Building Materials, 2012, 27(1):382-389. [5].李振国, 吉泽升, 李一珩. 氯氧镁水泥制品变形及开裂的研究进展[J]. 硅酸盐通报, 2012, 31(2):1-5. [6].DEMEDIUK T, COLE W F. Study of magnesium oxysulphase[J]. Australian Journal of Chemistry, 1957, 10 (3):287-294. [7].KHAN M Z N, SHAIKH F U A, HAO Y, et al. Synthesis of high strength ambient cured geopolymer composite by using low calcium fly ash[J]. Construction and Building Materials, 2016, 125:809-820. [8].邓德华. 提高镁式碱式盐水泥性能的理论与应用研究[D]. 长沙: 中南大学, 2005. [9].LI C D, YU H F. Influence of fly ash and silica fume on water-resistant property of magnesium oxychloride cement[J]. Journal of Wuhan University of Technology (Materials Science Edition), 2010, 25(4):721-724. [10].吴成友, 余红发, 文静, 等. 改性硫氧镁水泥物相组成及性能研究[J]. 新型建筑材料, 2013(5):68-72. [11].巴明芳, 王婕斐, 杨莹莹, 等. 改性硫氧镁胶凝材料的配制及性能研究[J]. 宁波大学学报(理工版), 2014, 27 (2):83-87. [12].LI Z G, CHEN S P, LI J Z. Influences of fly ash on the compressive strength and hydration products of magnesium oxysulfate cement[J]. Future Generation Communication and Networking, 2014, 41:139-141. [13].WU C, YU H F, DONG J, et al. Effects of material ratio, fly ash, and citric acid on magnesium oxysulfate cement [J]. ACI Materials, 2014, 111(3):291-297. [14].姜黎黎, 陈逸敏, 许可, 等. 粉煤灰对硫氧镁水泥抗压强度的影响[J]. 硅酸盐通报, 2015, 34(5):1427-1430. [15].CHAU C K, CHAN J, LI Z. Influences of fly ash on magnesium oxychloricle mortar[J]. Cement and Concrete Composites, 2009, 31(4):250-254. [16].METHA P K, MONTERIO P J M. Concrete: Structure, Properties and Materials[M]. New Jersey: Prentice Hall, 1993. |
| 备注/Memo: | 收稿日期: 2017?01?16. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 浙江省自然科学基金（LY17E080009）; 住建部科技项目（2014-K1-030）. 第一作者: 朱杰兆（1992－）, 男, 浙江舟山人, 在读硕士研究生, 主要研究方向: 高性能水泥基材料. E-mail: 554936851@qq.com *通信作者: 巴明芳（1975－）, 女, 山东滨州人, 博士/副教授, 主要研究方向: 高性能绿色建筑材料. E-mail: bamingfang@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |