密度泛函理论方法研究填料表面对聚合物摩擦化学的影响
PDF下载 (320)叶家鑫,孙 魏,刘小君,刘 焜.密度泛函理论方法研究填料表面对聚合物摩擦化学的影响[J].宁波大学学报(理工版),2021,34(6):28-35.DOI:
Ye Jiaxin,Sun Wei,Liu Xiaojun,Liu Kun.Effect of filler surface functionality on polymer tribochemistry using the density functional theory[J].Journal of Ningbo University(Natural Science & Engineering Edition),2021,34(6):28-35.DOI:
| Title: | Effect of filler surface functionality on polymer tribochemistry using the density functional theory |
| 作者: | 叶家鑫, 孙 魏, 刘小君, 刘 焜 |
| Author(s): | Ye Jiaxin, Sun Wei, Liu Xiaojun, Liu Kun |
| 关键词: | 高岭土; 聚四氟乙烯; 转移膜; 摩擦学性能; 摩擦化学 |
| Keywords: | kaolinite; polytetrafluoroethylene; transfer film; tribological properties; tribochemistry |
| 分类号: | TH117.3 |
| 文献标识码: | A |
| 摘要: | 采用超声分散法制备出氧化铝、高岭土、氧化硅/聚四氟乙烯复合材料, 使用线性往复摩擦磨损试验机对比三种复合材料的摩擦学性能. 结果表明 质量分数10%的氧化铝、高岭土能将聚四氟乙烯的磨损率降低约4个数量级, 而氧化硅仅能降低约3个数量级. 对金属对偶表面形成的转移膜的形貌和化学成分进行分析发现 氧化铝、高岭土/聚四氟乙烯在金属对偶面上形成了高度羧酸盐化的转移膜. 用密度泛函理论对三种填料表面上碳氟分子吸附过程进行模拟, 结果显示氧化铝、高岭土表面的路易斯酸性位点促进了碳氟分子的脱氟过程, 产生了更多的羧酸螯合物的中间产物; 氧化硅缺少路易斯酸性位点, 因此不能促进高度羧酸盐化的转移膜形成. |
| Abstract: | Alumina, kaolinite, and silica/polytetrafluoroethylene composites were prepared using the ultrasonic dispersion method. The tribological properties of the three composites were investigated using a linear reciprocating tribometer. The results showed that 10% mass fraction of alumina or kaolinite solely could reduce the wear rate of PTFE by about 4 orders of magnitude, while silica could only reduce it by about 3 orders of magnitude. Analysis of the morphology and chemical composition of the transfer films formed on the metal counterfaces revealed that alumina/polytetrafluoroethylene and kaolinite/polytetrafluoroethylene could form highly carboxylated transfer films. The adsorption of fluorocarbon molecules on the three filler surfaces were further simulated using density functional theory, which showed that the Lewis acidic sites on the surfaces of alumina and kaolinite promoted the defluorination of fluorocarbon molecules and the carboxylated chelation. The results showed that the Lewis acidic sites on the surfaces of alumina and kaolinite promoted the defluorination of fluorocarbon molecules and produced more intermediates for carboxylated transfer film formation, while silica lacked Lewis acidic sites and therefore could not promote the formation of carboxylated transfer films. |
| 参考文献 /References: | [1] Biswas S K, Vijayan K. Friction and wear of PTFE: A review[J]. Wear, 1992, 158(1/2):193-211. [2] 宫德利, 薛群基, 王弘立. PTFE基复合材料磨损机理的研究[J]. 固体润滑, 1989(2):88-94. [3] Tanaka K, Kawakami S. Effect of various fillers on the friction and wear of polytetrafluoroethylene-based composites[J]. Wear, 1982, 79(2):221-234. [4] 张招柱, 薛群基. 几种金属氧化物填充聚四氟乙烯复合材料在干摩擦条件下的摩擦磨损[J]. 摩擦学学报, 1997, 17(1):45-52. [5] Sun W, Liu X, Liu K, et al. Paradoxical filler size effect on composite wear: Filler–matrix interaction and its tribochemical consequences[J]. Tribology Letters, 2020, 68(4):131. [6] Burris D L, Sawyer W G. Improved wear resistance in alumina-PTFE nanocomposites with irregular shaped nanoparticles[J]. Wear, 2006, 260(7/8):915-918. [7] Kandanur S S, Rafiee M A, Yavari F, et al. Suppression of wear in graphene polymer composites[J]. Carbon, 2012, 50(9):3178-3183. [8] Krick B A, Ewin J J, McCumiskey E J. Tribofilm formation and run-in behavior in ultra-low-wearing polytetrafluoroethylene (PTFE) and alumina nanocomposites [J]. Tribology Transactions, 2014, 57(6):1058-1065. [9] Bhargava S, Makowiec M E, Blanchet T A. Wear reduction mechanisms within highly wear-resistant graphene- and other carbon-filled PTFE nanocomposites [J]. Wear, 2020, 444/445:203163. [10] Harris K L, Pitenis A A, Sawyer W G, et al. PTFE tribology and the role of mechanochemistry in the development of protective surface films[J]. Macromolecules, 2015, 48(11):3739-3745. [11] Onodera T, Kawasaki K, Nakakawaji T, et al. Effect of tribochemical reaction on transfer-film formation by poly (tetrafluoroethylene)[J]. The Journal of Physical Chemistry C, 2014, 118(22):11820-11826. [12] Burris D L, Sawyer W G. Tribological sensitivity of PTFE/alumina nanocomposites to a range of traditional surface finishes[J]. Tribology Transactions, 2005, 48(2): 147-153. [13] Khare H S, Moore A C, Haidar D R, et al. Interrelated effects of temperature and environment on wear and tribochemistry of an ultralow wear PTFE composite[J]. The Journal of Physical Chemistry C, 2015, 119(29): 16518-16527. [14] Khare H S, Burris D L. The extended wedge method: Atomic force microscope friction calibration for improved tolerance to instrument misalignments, tip offset, and blunt probes[J]. Review of Scientific Instruments, 2013, 84(5):055108. [15] 葛世荣, 张晓云. 钢-铜磨损过程中磨粒积聚的分形研究[J]. 摩擦学学报, 2001, 21(2):122-125. [16] K L, Sidebottom M A, Atkinson C C, et al. Ultralow wear PTFE-based polymer composites: The role of water and tribochemistry[J]. Macromolecules, 2019, 52(14):5268-5277. [17] Gonzalez J L, Ramirez R, Hallen J M, et al. Hydrogen- induced crack growth rate in steel plates exposed to sour environments[J]. Corrosion, 1997, 53(12):935-943. [18] Yuan Y X. A modified BFGS algorithm for unconstrained optimization[J]. IMA Journal of Numerical Analysis, 1991, 11(3):325-332. [19] Makinson K R, Tabor D. The friction and transfer of polytetrafluoroethylene[J]. Proceedings of the Royal Society of Series A: Mathematical and Physical Sciences, 1964, 281(1384):49-61. [20] Onodera T, K, Nakakawaji T, et al. Tribocatalytic reaction of polytetrafluoroethylene sliding on an aluminum surface[J]. The Journal of Physical Chemistry C, 2015, 119(28):15954-15962. [21] Lunkwitz K, Lappan U, Scheler U. Modification of perfluorinated polymers by high-energy irradiation[J]. Journal of Fluorine Chemistry, 2004, 125(6):863-873. [22] Puts G J, Crouse P, Ameduri B M. Polytetrafluoroethylene: Synthesis and characterization of the original extreme polymer[J]. Chemical Reviews, 2019, 119(3):1763-1805. [23] Przedlacki M, Kajdas C. Tribochemistry of fluorinated fluids hydroxyl groups on steel and aluminum surfaces[J]. Tribology Transactions, 2006, 49(2):202-214. [24] Sun W, Liu X, Song Q, et al. Mechanochemical effect of filler surface functionality on fluoropolymer tribology[J]. Macromolecules, 2021, 54(13):6417-6429. |
| 备注/Memo: | 收稿日期:2021-09-03.宁波大学学报（理工版）网址:http://journallg.nbu.edu.cn/ 基金项目:国家自然科学基金（51875152,51975174,51875153）;中央高校基本科研业务费专项资金（JZ2021HGPA0062）. 第一作者:叶家鑫（1987－）,男,安徽池州人,教授,主要研究方向:固体力学.E-mail:yejx@hfut.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |