PDF下载 (235)张丹蕾,王 胜,高 琦,郑哲溢,蔡章正,叶晓晨,巴明芳.重金属污泥高温处理磨细粉对改性硫氧镁水泥基材料性能的影响[J].宁波大学学报(理工版),2022,35(1):112-120.DOI:
ZHANG Danlei,WANG Sheng,GAO Qi,ZHENG Zheyi,CAI Zhangzheng,YE Xiaochen,BA Mingfang.Effects of high-temperature treatment of heavy metal sludge and ground powder on the performance of modified magnesium oxysulfide cement[J].Journal of Ningbo University(Natural Science & Engineering Edition),2022,35(1):112-120.DOI:
| Title: | Effects of high-temperature treatment of heavy metal sludge and ground powder on the performance of modified magnesium oxysulfide cement |
| 作者: | 张丹蕾, 王 胜, 高 琦, 郑哲溢, 蔡章正, 叶晓晨, 巴明芳 |
| Author(s): | ZHANG Danlei, WANG Sheng, GAO Qi, ZHENG Zheyi, CAI Zhangzheng, YE Xiaochen, BA Mingfang |
| 关键词: | 重金属污泥; 改性硫氧镁水泥基材料; 工作性能; 力学性能; 微细观结构 |
| Keywords: | heavy metal sludge; modified magnesium oxysulfide cement; working performance; mechanical properties; micro structure |
| 分类号: | TQ177.5 |
| 文献标识码: | A |
| 摘要: | 为探究重金属污泥高值资源化利用途径, 研究了含重金属污泥高温处理渣料磨细粉(简称磨细粉)对改性硫氧镁(MMOS)水泥基材料的工作性能、力学性能、早期自由收缩变形及其重金属浸出行为的影响. 结果表明: 随着磨细粉掺量的增加, MMOS水泥基材料的净浆流动度呈现逐渐增大趋势; 早期(3d)力学性能则呈现明显的降低趋势, 90d后磨细粉掺量对MMOS水泥基材料的力学性能的影响程度降低; 磨细粉可以显著降低MMOS水泥基材料早期的自由收缩变形值, 其中含10%磨细粉的MMOS水泥基材料早期的自由收缩变形比未掺加磨细粉MMOS水泥基材料的自由收缩变形值降低了57.1%. 微观分析结果表明: 掺加30%磨细粉后MMOS水泥基材料中水化产物5Mg(OH)2?MgSO4?7H2O(517相)的相对含量降低, MMOS水泥基材料硬化体的平均孔径提高了31.0%, 表明磨细粉降低了MMOS水泥基材料的力学性能. 当磨细粉掺量增加至40%时MMOS水泥基材料硬化体中重金属Ni、Cr、Zn和Cu的浸出浓度指标均能满足GB 30760-2014的浸出要求. |
| Abstract: | To explore the utilization of high-value resource such as heavy metal sludge, the effects of grinding powder of high temperature treated slag containing heavy metal sludge on the working performance, mechanical properties, early free shrinkage deformation, and heavy metal leaching behavior of modified magnesium sulfide oxide cement-based materials (MMOS) are investigated. The results show that with the increase of the content of ground powder, the net slurry fluidity of MMOS cement increases gradually, while its early mechanical properties decrease obviously. After 90-day observation, the effect of the content of ground powder on the mechanical properties of MMOS cement decreases. Grinding powder can significantly reduce the early free shrinkage deformation value of MMOS cement, in which the early free shrinkage deformation value of MMOS cement containing 10% ground powder decreases by 57.1% compared with the controlled sample. Micro- analysis results suggest that the relative content of hydration product 5Mg(OH)2?MgSO4?7H2O (517 phase) in MMOS cement decreases with the addition of ground powder, and the average pore size of the hardened body of MMOS cement increases by 31.0%, which explains why the ground powder reduces the mechanical properties of MMOS cement. Leaching concentrations of Ni, Cr, Zn, and Cu in hardened MMOS cement with grind powder content of 40% are all lower than the requirements of the standard GB 30760-2014. |
| 参考文献 /References: | [1] 刘海涛. 含重金属污泥的无害化处理技术研究[J]. 资源节约与环保, 2016(5):185; 187. [2] 宝志强. 利用污泥制备生态水泥的初步研究[D]. 杭州: 浙江大学, 2009. [3] Dai Z Q, Wu Y Q, Hu L C, et al. Evaluating physical-mechanical properties and long periods environmental risk of fired clay bricks incorporated with electroplating sludge[J]. Construction and Building Materials, 2019, 227:116716. [4] Kampala A, Horpibulsuk S. Engineering properties of silty clay stabilized with calcium carbide residue[J]. Journal of Materials in Civil Engineering, 2013, 25(5):632-644. [5] Zhang M T, Chen C, Mao L Q, et al. Use of electroplating sludge in production of fired clay bricks: Characterization and environmental risk evaluation[J]. Construction and Building Materials, 2018, 159:27-36. [6] Goyall A, Mensingerl M C, Barone S P, et al. Cement- Lock? process for waste management and energy recovery[EB/OL]. [2021-01-16]. https://www.witpress.com/Secure/elibrary/papers/WM02/WM02053FU.pdf. [7] dos Reis G S, Cazacliu B G, Cothenet A, et al. Fabrication, microstructure, and properties of fired clay bricks using construction and demolition waste sludge as the main additive[J]. Journal of Cleaner Production, 2020, 258:120733. [8] Jamuda H. Preparation of bricks using construction and demolition waste and sludge[EB/OL]. [2021-01-16]. http://ethesis.nitrkl.ac.in/6883/1/Preparation_Jamuda_2015.pdf. [9] 蒋华. 一种污泥建筑垃圾轻质免烧砖方法: CN104418574A[P]. 2017-04-19. [10] 秦玲. 硫氧镁水泥基轻质材料的制备与基本性能[D]. 哈尔滨: 哈尔滨工业大学, 2017. [11] 杨军彩. 改性剂对硫氧镁水泥性能的影响[J]. 混凝土, 2020(5):83-84; 93. [12] 陈方宇, 吴成友. 改性硫氧镁水泥性能研究[J]. 新型建筑材料, 2018, 45(6):56-58; 62. [13] 巴明芳, 朱杰兆, 柳俊哲. 早期温湿度条件对柠檬酸改性硫氧镁胶凝材料性能的影响及机理[J]. 材料导报, 2017, 31(20):107-113. [14] 王景然, 马保国, 李相国, 等. 磷酸镁水泥固化Pb2+、Zn2+、Cu2+及其水化产物研究[J]. 功能材料, 2014, 45(5):5060-5064. [15] GB/T 8077-2000. 混凝土外加剂均质性试验方法[S]. [16] GB/T 50082-2009. 普通混凝土长期性能和耐久性能试验方法标准[S]. [17] GB/T 1346-2011. 水泥基材料标准稠度用水量、凝结时间、安定性检验方法[S]. [18] GB/T 30810-2014. 水泥基材料胶砂中可浸出重金属的测定方法[S]. [19] 周璇, 孙南屏, 何健恒, 等. 废砂浆粉作为水泥混合材的基本性能试验研究[J]. 砖瓦, 2015(9):40-43. [20] GB 30760-2014. 水泥窑协同处置固体废物技术规范[S]. |
| 备注/Memo: | 收稿日期: 2021－03－15. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 国家自然科学基金（51978346）. 第一作者: 张丹蕾（1996－）, 女, 重庆江津人, 在读硕士研究生, 主要研究方向: 新型绿色建筑材料. E-mail: 1911083039@nbu.edu.cn *通信作者: 巴明芳（1975－）, 女, 山东滨州人, 博士/教授, 主要研究方向: 高性能绿色建筑材料. E-mail: bamingfang@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |