锆基电位型CO传感器的制备及其响应性能研究
PDF下载 (325)洪磊,金涵,孙寿通,简家文*.锆基电位型CO传感器的制备及其响应性能研究[J].宁波大学学报(理工版),2015,28(03):19-23.DOI:
HONG Lei,JIN Han,SUN Shou-tong,JIAN Jia-wen*.Research on Fabrication and Performance of Zirconia-based CO Sensor[J].Journal of Ningbo University(Natural Science & Engineering Edition),2015,28(03):19-23.DOI:
| Title: | Research on Fabrication and Performance of Zirconia-based CO Sensor |
| 作者: | 洪磊, 金涵, 孙寿通, 简家文* |
| Author(s): | HONG Lei, JIN Han, SUN Shou-tong, JIAN Jia-wen* |
| 关键词: | 电位型CO传感器 ; 敏感电极; 掺杂比例; 响应值; 敏感机理 |
| Keywords: | potentiometric CO sensor; sensing-electrode; ping ratio; sponse value; the sensing mechanism |
| 分类号: | TP212.2 |
| 文献标识码: | A |
| 摘要: | 为提高CO传感器的灵敏度, 采用丝网印刷技术制备了一系列以钇稳定氧化锆为固体电解质、以ZnO材料中掺杂不同比例的In2O3为敏感电极、以Pt为参比电极的片式结构电位型CO传感器, 并于特定的工作条件下测试其对不同气体组分的响应性能. 结果表明, 当掺杂比例为质量分数0.3, 烧结温度为1200℃且工作温度为500℃时, 传感器对CO气体的响应值最大, 达到-59mV, 接近未掺杂前的2倍, 传感器的灵敏度有很大提高. 并为阐述传感器的敏感机理, 开展了相应的材料结构表征(XRD/SEM)和电化学催化活性(阻抗谱)测试研究. |
| Abstract: | To improve the sensitivity of CO sensor, several plate structure potential sensors are prepared using screen-printing technology. The process is operated on yttria-stablilzed zirconia, taking ZnO materials doped with different proportion of In2O3 as the sensing electrode and Pt as the reference electrode. The sensing characteristics of these sensors are evaluated under fixed conditions. The results indicate that the response reaches the largest in value with the doping ratio being 30 wt.%, sintering temperature being 1200℃ and working temperature being 500℃, which reaches -59mV, nearly twice as much as that before doped, suggesting the significantly improved sensitivity of the sensor. Finally, a series of characterization methods such as SEM, XRD as well as the evaluation of the electrochemical catalytic activity (refers to impedance spectroscopy) are adopted to establish the correlation between the microstructure of the SEs, based on which the working principle of the sensor is illustrated in detail |
| 参考文献 /References: | [1].Miura N, Raisen T, Lu Geyu, et al. Highly selective CO sensor using stabilized zirconia and a couple of oxide electrodes[J]. Sensors and Actuators B, 1998, 47:84-91. [2].Fergus J W. Solid electrolyte based sensors for the measurement of CO and hydrocarbon gases[J]. Sensors and Actuators B: Chemical, 2007, 122:683-693. [3].王常珍. 固体电解质和化学传感器[M]. 北京: 冶金工业出版社, 2000:33-56. [4].Patil D R, Patil L A. Cr2O3-modified ZnO thick film resistors as LPG sensors[J]. Talanta 2009, 77:1409-1414[J]. 传感技术学报, 2011, 24(7):954-958. [5].Jin Han, Huang Youju, Jian Jiawen. Plate-like Cr2O3 for highly selective sensing of nitric oxide[J]. Sensors and Actuators B. 2015, 206:107-110. [6].周贞, 简家文, 吴翔等. CO气体对极限电流型氧传感器特性的影响[J]. 传感器与微系统, 2012, 31(5):20-22. [7].Xiao Junjia, Chen Biaohua, Liang Xin, et al. NiO microspheres with tunable porosity and morphology effects for CO oxidation[J]. Catal Sci Technol, 20111): 999-1005. [8].高建元, 邹杰, 章东兴, 等. 氧气对NOx传感器气敏特性的影响[J]. 传感技术学报, 2010, 23(9):1215-1219. [9].罗志安, 肖建中, 固态混合电势气体传感器的原理和应用[J]. 传感器世界, 2005, 11(8):17-20.Iio A, Ikeda H, Miura N, et al. Potentiometric YSZ-based oxygen sensor using BaFeO3 sensing electrode[J]. Elec- trochemistry Communications, 2014, 11(48):134-137. [10].简家文, 高建元, 邹杰. NiO/YSZ结构NO传感器的敏感特性[J]. 硅酸盐学报, 2010, 38(6):1036-104 |
| 备注/Memo: | 收稿日期: 2015?01?05. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 国家自然科学基金（61471210）; 浙江省科技厅重大科技专项重点工业项目（2011C16037）; 宁波市自然科学基金（2013A610002）. 第一作者: 洪磊（1990－）, 男, 安徽合肥人, 在读硕士研究生, 主要研究方向: 锆基气敏传感器. E-mail: hongshaolong@126.com *通信作者: 简家文（1967－）, 男, 河南淮滨人, 教授, 主要研究方向: 气体敏感材料. E-mail: jianjiawen@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |