Ph-ATP@PANI复合材料的制备及防腐性能研究
PDF下载 (439)邹 挺1,2,刘丰华1*,肖通虎2,许高杰1.Ph-ATP@PANI复合材料的制备及防腐性能研究[J].宁波大学学报(理工版),2016,29(3):72-77.DOI:
ZOU Ting1,2,LIU Feng-hua1*,XIAO Tong-hu2,XU Gao-jie1.Preparation and Anticorrosion of Ph-ATP@PANI Nanocomposites[J].Journal of Ningbo University(Natural Science & Engineering Edition),2016,29(3):72-77.DOI:
| Title: | Preparation and Anticorrosion of Ph-ATP@PANI Nanocomposites |
| 作者: | 邹 挺1, 2, 刘丰华1*, 肖通虎2, 许高杰1 |
| Author(s): | ZOU Ting1, 2, LIU Feng-hua1*, XIAO Tong-hu2, XU Gao-jie1 |
| 关键词: | 凹凸棒石; 硅烷改性; 聚苯胺; 防腐 |
| Keywords: | attapulgite; silicane modification; polyaniline; anticorrosion |
| 分类号: | O64 |
| 文献标识码: | A |
| 摘要: | 以苯基-三乙氧基硅烷改性纳米凹凸棒石(Ph-ATP)为载体, 通过原位聚合制备了Ph- ATP@PANI纳米复合材料, 通过红外光谱(FTIR)、热重分析(TGA)、扫描电镜(SEM)和透射电镜(TEM)等表征了复合材料的微观结构和形貌. 以Ph-ATP@PANI纳米复合材料为填料制备了Ph-ATP@PANI/环氧树脂防腐涂层, 用电化学阻抗谱(EIS)、极化曲线(Tafel)以及盐雾试验分析了涂层的防腐性能. 测试结果表明, 相比纯PANI, Ph-ATP@PANI复合材料中PANI的红外特征吸收峰蓝移、热分解温度降低, Ph-ATP@PANI粒子在环氧树脂涂层中的分散性增强, 涂层的防腐蚀性能显著提升. |
| Abstract: | The Ph-ATP@PANI nanocomposites are prepared via in-situ-polymerization using the phenyltriethoxysilane-modified attapulgite as the core. The structure and morphology of the Ph-ATP@PANI nanocomposites are investigated with FTIR, TGA, SEM and TEM. The anticorrosive coating is prepared by introducing the Ph-ATP@PANI to the epoxy resin. The antiseptic properties are characterized with electrochemical impedance spectroscopy (EIS), polarization curve (Tafel) and salt spray test. The results indicate that the infrared absorption peaks of PANI in Ph-ATP@PANI become blue shift and the thermal decomposition temperature decrease. Compared with the pure PANI, the dispersion and anti-corrosion performance of the Ph-ATP@PANI are significantly enhanced. |
| 参考文献 /References: | [1].DEBERRY D W. Modification of the electrochemical and corrosion behavior of stainless steels with an electroactive coating[J]. Journal of the Electrochemical Society, 1985, 132(5):1022-1026. [2].CHANG C H, HUANG T C, PENG C W, et al. Novel anticorrosion coatings prepared from polyaniline/ graphene composites[J]. Carbon, 2012, 50(14):5044-5051. [3].YEH J M, LIOU S J, LAI C Y, et al. Enhancement of corrosion protection effect in polyaniline via the formation of polyaniline-clay nanocomposite materials[J]. Chemistry of Materials, 2001, 13(3):1131-1136. [4].WANG W B, WANG F F, KANG Y R, et al. Facile self-assembly of Au nanoparticles on a magnetic attapulgite/Fe3O4 composite for fast catalytic decoloration of dye[J]. Rsc Advances, 2013, 3(29):11515-11520. [5].XU J X, WANG W B, WANG A Q. Effects of solvent treatment and high-pressure homogenization process on dispersion properties of palygorskite[J]. Powder Technology, 2013, 235:652-660. [6].曾永斌, 姚超, 丁永红, 等. 盐酸掺杂聚苯胺/凹凸棒土纳米导电复合材料的研究[J]. 非金属矿, 2008, 31(4): 53-56. [7].吴凤芹, 曾永斌, 姚超, 等. SSA-PANI/ATP导电纳米复合材料的制备和表征[J]. 涂料工业, 2008, 38(12):7- 11. [8].HOU W P, LIU Y, GE Z Y, et al. Comparison study on anticorrosion performances of the epoxy coatings with two different nano-polyanilines for Q235 steel[J]. Materials and Corrosion, 2013, 64(11):960-968. [9].CHEN L F, LIANG H W, LU Y, et al. Synthesis of an attapulgite clay@carbon nanocomposite adsorbent by a hydrothermal carbonization process and their application in the removal of toxic metal ions from water[J]. Langmuir, 2011, 27(14):8998-9004. [10].JITIANU A, GONZALEZ G, KLEIN L C. Hybrid sol-gel glasses with glass-transition temperatures below room temperature[J]. Journal of the American Ceramic Society, 2015, 98(12):3673-3679. [11].ZHANG Z M, WEI Z X, WAN M X. Nanostructures of polyaniline doped with inorganic acids[J]. Macromolecules, 2002, 35(15):5937-5942. [12].ZHU L, LIU P, WANG A Q. High clay-content attapulgite/poly(acrylic acid) nanocomposite hydrogel via surface-initiated redox radical polymerization with modified attapulgite nanorods as initiator and cross- linker[J]. Industrial & Engineering Chemistry Research, 2014, 53(5):2067-2071. [13].PAN Y Z, XU Y, LI A, et al. Hybrid network structure and mechanical properties of rodlike silicate/cyanate ester nanocomposites[J]. Macromolecules, 2008, 41(23):9245- 9258. [14].TIAN G Y, KANG Y R, MU B, et al. Attapulgite modified with silane coupling agent for phosphorus adsorption and deep bleaching of refined palm oil[J]. Adsorption Science & Technology, 2014, 32(1):37-48. [15].HUANG H Y, HUANG T C, YEH T C, et al. Advanced anticorrosive materials prepared from amine-capped aniline trimer-based electroactive polyimide-clay nanocomposite materials with synergistic effects of redox catalytic capability and gas barrier properties[J]. Polymer, 2011, 52(11):2391-2400. [16].RADHAKRISHNAN S, SIJU C R, MAHANTA D, et al. Conducting polyaniline-nano-TiO2 composites for smart corrosion resistant coatings[J]. Electrochimica Acta, 2009, 54(4):1249-1254. |
| 备注/Memo: | 收稿日期: 2016?04?08. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 国家自然科学基金（21203225）; 浙江省自然科学基金（LQ12A04005）; 江苏省科技支撑计划（BE2013082）. 第一作者: 邹挺（1991－）, 男, 浙江宁波人, 在读硕士研究生, 主要研究方向: 纳米复合材料. E-mail: zouting@nimte.ac.cn *通信作者: 刘丰华（1981－）, 男, 湖南沅江人, 副研究员, 主要研究方向: 软纳米功能材料. E-mail: lfh@nimte.ac.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |