PDF下载 (285)李正辉,徐卫红,胡敏杰,谢晨光,高浩其,房江华.甲基丙烯酸甲酯第三单体对于稀土催化降冰片烯与苯乙烯共聚的影响[J].宁波大学学报(理工版),2016,29(4):82-85.DOI:
LI Zheng-Hui,XU Wei-hong,HU Min-jie,XIE Chen-guang,GAO Hao-qi,FANG Jiang-hua.Effect of Methyl Methacrylate as a Third Monomer on Copolymerization of Norbornene and Styrene Catalyzed by Nd(naph)3-Al(i-Bu)3[J].Journal of Ningbo University(Natural Science & Engineering Edition),2016,29(4):82-85.DOI:
| Title: | Effect of Methyl Methacrylate as a Third Monomer on Copolymerization of Norbornene and Styrene Catalyzed by Nd(naph)3-Al(i-Bu)3 |
| 作者: | 李正辉, 徐卫红, 胡敏杰, 谢晨光, 高浩其, 房江华 |
| Author(s): | LI Zheng-Hui, XU Wei-hong, HU Min-jie, XIE Chen-guang, GAO Hao-qi, FANG Jiang-hua |
| 关键词: | 环烷酸钕; 三异丁基铝; 降冰片烯; 苯乙烯; 甲基丙烯酸甲酯 |
| Keywords: | neodymium naphthenate; triisobuytl aluminum; norbornene; styrene; methyl methacrylate |
| 分类号: | O631.5 |
| 文献标识码: | A |
| 摘要: | 随着甲基丙烯酸甲酯第三单体的加入, 可以大大地提高Nd(naph)3-Al(i-Bu)3(naph=环烷酸)稀土系催化剂催化降冰片烯与苯乙烯共聚产物的分子量, 并使分子量分布变窄. 文中采用凝胶渗透色谱、核磁共振和红外光谱方法证明了三元共聚物的合成, 并研究了不同反应条件下对于聚合的影响. 结果表明: 稀土催化剂在温和的反应条件下有较好的催化性能, 并且共聚物分子量分布较小. |
| Abstract: | Adding the third monomer methyl methacrylate can greatly increase the molecular weight of the copolymerization product of norbornene and styrene catalyzed by rare earth-based catalyst Nd(naph)3-Al(i-Bu)3 (naph=naphthenate), and can narrow the molecular weight distribution. With gel permeation chromatography, the nuclear magnetic resonance and infrared spectroscopy the synthesis of terpolymer is accomplished under the reaction condition for the polymerization. The results demonstrate that, under mild reaction condition, the rare earth catalyst possesses the better catalytic properties, and the molecular weight distribution of the copolymer is small. |
| 参考文献 /References: | [1] KAIMOTO Y, NOZAKI K, TAKECHI S, et al. Alicyclic polymer for ArF and KrF excimer resist based on chemical ampli?cation[J]. Proc SPIE, 1992, 1672:66-73. [2] BARAD S E, GREINERT N, SEN A, et al. Copoly- merization of methyl acrylate with norbornene derivatives by atom transfer radical polymerization[J]. Macromole- cules, 2002, 35:7521-7526. [3] CHEN Y, SEN A. Effect of Lewis acids on reactivity ratios for (meth)acrylate/nonpolar alkene copolymerize- tions[J]. Macromolecules, 2009, 42(12):3951-3957. [4] TORIUMI M, SHIDA N, YAMAZAKI T, et al. Fluoropolymer-based resist materials for 157-nm lithograph[J]. Microelectronic Engineering, 2002, 61/62: 717-722. [5] HUANG C F, WANG S K, KUO S W, et al. Homopoly- merization and copolymerization of tert-butyl methacry- late and norbornene with nickel-based methylalumino- xane catalysts[J]. J Appl Polym Sci, 2004, 92:1824-1833. [6] WANG L Y, LI Y F, ZHU F M, et al. Copolymerization of norbornene and methyl acrylate by b-ketoiminato palladium complexes[J]. Polymer Bulletin, 2006, 57: 73-81. [7] SZUROMI E, SHEN H, GOODALL B L, et al. Polyme- rization of norbornene and methyl acrylate by a bimetallic palladium(II) allyl complex[J]. Organometallics, 2008, 27: 402-409. [8] FENG Q, CHEN D, FENG D Y, et al. Synthesis of poly(norbornene-co-styrene) copolymers containing high styrene incorporation using bis(β-ketoamino) copper catalysts[J]. J Polym Res, 2014, 21:497-503. [9] 房江华, 黄士力, 沈之荃. Nd(naph)3-Al(i-Bu)3催化邻苯二甲酸酐与环氧丙烷交替共聚[J]. 催化学报, 1998, 19(1):92-94. [10] 房江华, 罗云杰. 丙烯酸丁酯在Nd-Al-α, α, -联吡啶催化体系中聚合[J]. 宁波大学学报(理工版), 1999, 12(3): 29-32. [11] 徐卫红, 胡敏杰, 李正辉, 等. 稀土催化降冰片稀与苯乙烯、丙烯酸丁酯三元共聚[J]. 宁波工程学院学报, 2015, 27(4):1-4. |
| 备注/Memo: | 收稿日期: 2016－03－01. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 宁波市自然科学基金（2014A610133）; 宁波市有机高分子创新团队项目. 第一作者: 李正辉（1981－）, 男, 安徽淮北人, 博士/讲师, 主要研究方向: 高分子合成及材料改性加工. E-mail: lzhnut@163.com 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |