PDF下载 (343)姜 瀚,余 丰,李淑欣,苏云帅.GCr15马氏体钢剪切试样断口局部熔融研究[J].宁波大学学报(理工版),2021,34(4):61-66.DOI:
JIANG Han,YU Feng,LI Shuxin,SU Yunshuai.Localized melting on fracture surface of shear-dominated specimen of GCr15 martensite steel[J].Journal of Ningbo University(Natural Science & Engineering Edition),2021,34(4):61-66.DOI:
| Title: | Localized melting on fracture surface of shear-dominated specimen of GCr15 martensite steel |
| 作者: | 姜 瀚, 余 丰, 李淑欣, 苏云帅 |
| Author(s): | JIANG Han, YU Feng, LI Shuxin, SU Yunshuai |
| 关键词: | GCr15马氏体钢; 剪切压缩试样; 局部熔融; 剪切塑性应变 |
| Keywords: | GCr15 martensite steel; shear-compression specimen; localized melting; shear plastic strain |
| 分类号: | TG113 |
| 文献标识码: | A |
| 摘要: | 本文采用开45?缺口剪切压缩试样, 比较研究GCr15马氏体钢在准静态压缩和高速冲击下样品断裂面的温升机制. 结果显示两种加载状态的断口上都发现了大量的局部熔融, 说明温升均超过1500℃. GCr15马氏体钢的塑性很低, 然而在剪切应力主导的试样上, 两种加载的剪切面均发生了很大塑性应变. 试样断裂瞬时所释放的能量以及裂纹面间的大滑移摩擦导致局部温升超过熔点. 分析结果表明, 两种加载模式下产生的熔融物均由残余奥氏体和孪晶马氏体组成. 受热的影响, 熔融物下面的基体组织经历了动态再结晶, 从而形成马氏体和奥氏体等轴晶. 因此,在剪应力主导的应力状态下, 马氏体钢的剪切断裂机理与加载速率无关, 高速冲击与准静态加载下的断裂模式和机理没有本质区别. 断裂瞬间产生局部温升促使材料熔融, 这是该材料剪切断裂的特性. 本文结论对GCr15马氏体钢剪切主导断裂机理的认识有重要意义. |
| Abstract: | In this study, quasi-static compression and high-rate impact tests are conducted on shear-compression specimens with 45? notch to investigate the temperature rise mechanism at fracture. The results showed that considerable localized melting is observed on fracture surfaces of two loading cases, indicating the temperature rise over 1500℃. The plasticity of GCr15 martensite steel is very low. However, large plastic strain occurs at the shear plane in the shear-dominated specimens. At fracture, the energy released by crack propagation combined with large sliding friction leads to localized temperature rise up to the melting point. The results show that the melt produced under the two loading modes is composed of residual austenite and twin martensite. Below the melt, the matrix is severely heat-affected and subjected to dynamic recrystallization. It is composed of equiaxed austenite and martensite. It suggests that the shear fracture of this material is independent of loading rates. The fracture mode and mechanism under dynamic loading such as high strain impact makes no difference to the quasi-static loading. Localized melting at the moment of fracture is a common feature in this material. This study is of great significance in understanding the shear-dominated fracture mechanism of GCr15martensite steel. |
| 参考文献 /References: | [1] Kapoor R, Nemat-Nasser S. Determination of temperature rise during high strain rate deformation[J]. Mechanics of Materials, 1998, 27(1):1-12. [2] 孙秀荣, 王会珍, 杨平, 等. 不同结构金属高速压缩力学行为及微观剪切结构差异[J]. 金属学报, 2014, 50(4):387-394. [3] Guo Y Z, Ruan Q C, Zhu S X, et al. Temperature rise associated with adiabatic shear band: Causality clarified[J]. Physical Review Letters, 2019, 122:015503. [4] Xu Z, Liu Y, Sun Z, et al. On shear failure behaviors of an armor steel over a large range of strain rates[J]. International Journal of Impact Engineering, 2018, 118:24-38. [5] Li N, Wang Y D, Lin P R, et al. Localized amorphism after high-strain-rate deformation in TWIP steel[J]. Acta Materialia, 2011, 59(16):6369-6377. [6] Qu R T, Zhang Z F. Compressive fracture morphology and mechanism of metallic glass[J]. Journal of Applied Physics, 2013, 114(19):193504. [7] Huang K, Logé R E. A review of dynamic recrystallization phenomena in metallic materials[J]. Materials & Design, 2016, 111:548-574. [8] Rittel D, Lee S, Ravichandran G. A shear-compression specimen for large strain testing[J]. Experimental Mechanics, 2002, 42(1):58-64. [9] Giovanola J H. Adiabatic shear banding under pure shear loading. Part II: Fractographic and metallographic observations[J]. Mechanics of Materials, 1988, 7(1):73-87. [10] Sakai T, Belyakov A, Kaibyshev R, et al. Dynamic and post-dynamic recrystallization under hot, cold and severe plastic deformation conditions[J]. Progress in Materials Science, 2014, 60(1):130-207. [11] Su Y S, Li S X, Yu F, et al. Revealing the shear band origin of white etching area in rolling contact fatigue of bearing steel[J], International Journal of Fatigue, 2021, 142:105929. [12] Liu J X, Li S K, Zhou X Q, et al. Adiabatic shear banding in a tungsten heavy alloy processed by hot-hydrostatic extrusion and hot torsion[J]. Scripta Materialia, 2008, 59(12):1271-1274. [13] Armstrong R W, Coffey C S, Elban W L. Adiabatic heating at a dislocation pile-up avalanche[J]. Acta Metallurgica, 1982, 30(12):2111-2116. [14] Makel D D, Wilsdorf H G F. Localized melting at separation of AISI 4340 steel tensile samples[J]. Materials Science and Engineering A, 1991, 142(1):107-114. [15] Makel D D, Wilsdorf H G F. An investigation of unusual surface features caused by adiabatic shear during tensile separation[J]. Scripta Metallurgica, 1987, 21(9):1229-1234. [16] Kuhlmann-Wilsdorf D. Theory of melting[J]. Physics Letters, 1965, 17(2):113-114. [17] Armstrong R W, Walley S M. High strain rate properties of metals and alloys[J]. International Materials Reviews, 2008, 53(3):105-128. [18] Yang F, Li C H, Cheng S W, et al. Deformation behavior of explosive detonation in electroformed nickel liner of shaped charge with nano-sized grains[J]. Transactions of Nonferrous Metals Society of China, 2010, 20(8):1397-1402. [19] Holt W H, Mock W, Soper W G, et al. Reverse-ballistic impact study of shear plug formation and displacement in Ti6Al4V alloy[J]. Journal of Applied Physics, 1993, 73(8):3753-3759. [20] Fras T, Roth C C, Mohr D. Fracture of high-strength armor steel under impact loading[J]. International Journal of Impact Engineering, 2018, 111:147-164. [21] Makel D D, Eylon D. The effect of microstructure on localized melting at separation in Ti-6Al-4V tensile samples[J]. Metallurgical Transactions A, 1990, 21(12):3127-3136. |
| 备注/Memo: | 收稿日期: 2020－12－18. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 国家自然科学基金（51675287, 52075271）; 宁波市自然科学基金（2019A610172）; 浙江省教育厅科研项目（Y201940908）. 第一作者: 姜瀚（1995－）, 男, 浙江宁波人, 在读硕士研究生, 主要研究方向: 机械结构强度. E-mail: 1491275843@qq.com *通信作者: 余丰（1982－）, 男, 浙江宁波人, 讲师, 主要研究方向: 材料和结构强度. E-mail: yufeng1@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |