纤维改性硫氧镁基仿木保温材料性能研究
PDF下载 (352)许浩锋,翟灵杰,胡 凯,刘静涵,陈邦玺,巴明芳.纤维改性硫氧镁基仿木保温材料性能研究[J].宁波大学学报(理工版),2020,33(2):60-65.DOI:
XU Haofeng,ZHAI Lingjie,HU Kai,LIU Jinghan,CHEN Bangxi,BA Mingfang.Properties of fiber modified magnesium oxysulfate based wood-like thermal insulation material[J].Journal of Ningbo University(Natural Science & Engineering Edition),2020,33(2):60-65.DOI:
| Title: | Properties of fiber modified magnesium oxysulfate based wood-like thermal insulation material |
| 作者: | 许浩锋, 翟灵杰, 胡 凯, 刘静涵, 陈邦玺, 巴明芳 |
| Author(s): | XU Haofeng, ZHAI Lingjie, HU Kai, LIU Jinghan, CHEN Bangxi, BA Mingfang |
| 关键词: | 硫氧镁水泥; 仿木保温材料; 抗裂性; 纤维 |
| Keywords: | magnesium oxy sulfate cement; wood-like thermal insulation materials; crack resistance; fiber |
| 分类号: | TU528 |
| 文献标识码: | A |
| 摘要: | 为了提高硫氧镁基仿木保温材料的各项性能, 分别研究了相同长度的聚丙烯纤维(PPF)、聚乙烯醇纤维(PVAF)、玻璃纤维(GF)对其性能的影响. 结果表明: 随着纤维掺量的增加, 硫氧镁基仿木保温材料的流动性有所降低; GF对其抗压抗折强度的提高效果最明显, 其中GF掺量为1.0 kg·m-3时早期抗压强度最高, PVAF掺量为0.5 kg·m-3时其早期抗压强度最高; PPF明显提高了硫氧镁基仿木保温材料的耐水性, 其掺量为0.5 kg·m-3时软化系数最大, 而GF掺量在1.0 kg·m-3时, 浸水软化系数稍高于未加纤维的对比试件; 掺加PVAF后硫氧镁基保温材料的导热系数出现一定程度的降低, 其中PVAF掺量在1.5 kg·m-3时其导热系数最低. GF和PPF可以明显地降低硫氧镁基仿木保温材料的收缩值, 其中GF降低自收缩效果较好, 而PPF可以明显地降低其干燥收缩值. |
| Abstract: | In order to improve the properties of magnesium oxy sulfate based wood-like thermal insulation materials, the effects of fiber modification with polypropylene fiber (PPF), polyvinyl alcohol fiber (PVAF) and glass fiber (GF) in same length were studied in this paper. The results show that the fluidity of magnesium oxy sulfate cement based wood-like thermal insulation material decreases with the increase of fiber content; GF has the most obvious effect on the improvement of its compressive and flexural strength; the early compressive strength is the highest when the content of GF is 1.0 kg·m-3, and it is the highest when the content of PVAF is 0.5 kg·m-3; PPF obviously improves the water resistance of magnesium oxy sulfate cement based wood-like thermal insulation material. The softening coefficient of wood-like thermal insulation material is the highest when the content of PPF is 0.5 kg·m-3, and it is slightly higher than that of the unfibered comparative test piece when the content of GF is 1.0 kg·m-3. The thermal conductivity of wood-like thermal insulation material decreases to a certain extent, which is the lowest when the content of PVAF is 1.5 kg·m-3. The results also show that GF and PPF can obviously reduce the shrinkage value of magnesium oxy sulfate based thermal insulation materials. GF reduces the auto-shrinkage better, while PPF significantly reduces the drying shrinkage value. |
| 参考文献 /References: | [1] 刘晓娜, 薛硕, 王晓欢, 等. 面板种类和芯板厚度对结构用木质保温板力学性能的影响[J]. 木材工业, 2018, 32(4):9-13. [2] Structural Timber Association. Timber engineering notebook series: No.10: Structural insulated panel construction[J]. Structural Engineer Journal of the Institution of Structural Engineer, 2015, 9(3):40-46. [3] Panjehpour M, Ali A A A, Voo Y L. Structural insulated panels: Past, present, and future[J]. Journal of Engineering Project and Production Management, 2013, 3(1):2-8. [4] 马成良, 贾志峰, 郭建国, 等. 新型无机轻骨料防火保温板[J]. 消防科学与技术, 2013, 32(10):1134-1136. [5] 李连勇, 岳建伟, 来强. 保温抗裂砂浆性能试验研究[J]. 河南大学学报(自然科学版), 2011, 41(2):214-216. [6] 陈松和, 杨杰, 尹刚, 等. 外保温抗裂抹面砂浆性能提升研究[J]. 低温建筑技术, 2015, 37(12):15-17. [7] 葛松. 钙钒石补偿硅酸盐水泥硬化收缩的理论估算[J]. 山西建筑, 2010, 36(31):158-159. [8] 李明跃. 膨胀珍珠岩氯氧镁胶凝材料及其应用的研究[D]. 合肥: 合肥工业大学, 2014. [9] Xu B, Ma H, Hu C et al. Influence of curing regimes on mechanical properties of magnesium oxychloride cement-based composites[J]. Construction and Building Materials, 2016, 102(1):613-619. [10] He P, Poon C S, Tsang D C W. Comparison of glass powder and pulverized fuel ash for improving the water resistance of magnesium oxychloride cement[J]. Cement and Concrete Composites, 2018, 86:98-109. [11] Li Z, Chau C K. Influence of molar ratios on properties of magnesium oxychloride cement[J]. Cement and Concrete Research, 2007, 37(6):866-870. [12] 李颖, 余红发, 董金美, 等. 氯氧镁胶凝材料吸潮返卤泛霜的研究进展[J]. 硅酸盐通报, 2010, 29(4):858-865. [13] 马慧, 关博文, 王永维, 等. 氯氧镁水泥胶凝材料的研究进展[J]. 材料导报, 2015, 29(15):103-107. [14] 陈雪霏. 氯氧镁水泥耐水复合改性的研究[D]. 镇江: 江苏大学, 2017. [15] 张翠苗, 杨红健, 马学景. 氯氧镁水泥的研究进展[J]. 硅酸盐通报, 2014, 33(1):117-121. [16] 王海平, 肖学英, 王继东, 等. 外加剂对硫氧镁水泥的改性作用[J]. 盐湖研究, 2013, 21(1):44-49. [17] 李国栋, 毕万利, 孙恩禹, 等. 改性硫氧镁水泥的配制及性能研究[J]. 耐火材料, 2016, 50(6):469-472. [18] 秦玲. 硫氧镁水泥基轻质材料的制备与基本性能[D]. 哈尔滨: 哈尔滨工业大学, 2017. [19] 吴成友, 余红发, 文静, 等. 改性硫氧镁水泥物相组成及性能研究[J]. 新型建筑材料, 2013, 40(5):68-72. [20] 王明英, 张兴福, 王自福, 等. 改性硫氧镁胶凝材料原材料配比的研究[J]. 新型建筑材料, 2016, 43(6):6-8. [21] 陆建兵, 朱晓华, 张童童, 等. 改性硫氧镁水泥的性能研究[J]. 混凝土与水泥制品, 2016(9):24-28. [22] 朱杰兆, 薛涛, 巴明芳. 高抗折硫氧镁基无机复合胶凝材料的制备及其机理[J]. 宁波大学学报(理工版), 2017, 30(6):66-72. [23] 司雯, 曹明莉, 冯嘉琪. 纤维增强水泥基复合材料的流动性与流变性研究进展[J]. 材料导报, 2019, 33(5):819- 825. [24] 赵国藩, 彭少民, 黄承逵. 钢纤维混凝土结构[M]. 北京: 中国建筑工业出版社, 1999. [25] 张悦. 聚丙烯纤维混凝土力学性能及损伤破坏形态研究[D]. 西安: 西安理工大学, 2019. [26] 寇长珍. 碳纳米管—玻璃纤维共掺杂改性环氧复合材料绝缘及导热性能研究[D]. 西安: 西安理工大学, 2018. [27] 龚建清, 周孜豪. 纤维和外加剂对泡沫混凝土收缩性能的影响[J]. 湖南大学学报(自然科学版), 2019, 46(5): 76-85. |
| 备注/Memo: | 收稿日期: 2019－05－06. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 浙江省自然科学基金（LY17E080009）. 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/第一作者: 许浩锋（1995－）, 男, 浙江台州人, 在读硕士研究生, 主要研究方向: 水泥基复合材料. E-mail: 761383760@qq.com *通信作者: 巴明芳（1975－）, 女, 山东滨州人, 博士/副教授, 主要研究方向: 高性能绿色建筑材料. E-mail: bamingfang@nbu.edu.cn |