PDF下载 (340)林 楠,江乐鑫,杨梦娜,柳俊哲.水泥浆体中氯盐阳离子种类对游离氯离子浓度的影响[J].宁波大学学报(理工版),2020,33(4):77-81.DOI:
LIN Nan,JIANG Lexin,YANG Mengna,LIU Junzhe.The influence of chloride cation type on the concentration of free chloride ion in cement paste[J].Journal of Ningbo University(Natural Science & Engineering Edition),2020,33(4):77-81.DOI:
| Title: | The influence of chloride cation type on the concentration of free chloride ion in cement paste |
| 作者: | 林 楠, 江乐鑫, 杨梦娜, 柳俊哲 |
| Author(s): | LIN Nan, JIANG Lexin, YANG Mengna, LIU Junzhe |
| 关键词: | 水泥基材料; 阳离子类型; 游离氯离子浓度; 钙矾石; 氯盐掺量 |
| Keywords: | cement-based materials; cation types; free chloride ion concentration; ettringite; chloride content |
| 分类号: | TU528.0 |
| 文献标识码: | A |
| 摘要: | 研究了不同阳离子氯盐作用下, 水泥净浆中游离氯离子浓度和结合氯离子浓度的变化, 并通过X射线衍射技术和电镜扫描分析技术观察其微观状态. 结果表明: 掺氯化钠的试件中游离氯离子浓度更高, 钙离子对氯离子的结合能力更强; 氯化钙比氯化钠更易与水泥熟料发生反应, 生成水化产物Friendel复盐和C-S-H凝胶; 掺氯化钙的试块表面晶体更为细密且结构多样. |
| Abstract: | The change of the concentration of free chloride ion and combined chloride ion in cement paste is investigated under the reaction of different cationic chloride salts. The results suggest that the concentration of free chloride ions reads higher in the sample mixed with sodium chloride, and the binding force of calcium ions to chloride ions turns out to be stronger. Calcium chloride reacts with cement clinker more easily than sodium chloride to produce Friendel compound salt and C-S-H gel. The crystals on the surface of the test piece doped with calcium chloride are more compact and possess various structures. |
| 参考文献 /References: | [1] Honore T, Okeil A M, Castaneda H, et al. A framework for reliability assessment of corrosion damaged reinforced concrete structures[C]. 2018世界交通运输大会, 北京, 2018. [2] 钟亚伟, 李固华. 沿海混凝土耐久性研究综述[J]. 四川建筑科学研究, 2007, 33(1):90-95. [3] Zhao Y X, Dong J F, Wu Y Y, et al. Steel corrosion and corrosion-induced cracking in recycled aggregate concrete[J]. Corrosion Science, 2014, 85:241-250. [4] Muthulingam S, Rao B N. Non-uniform corrosion states of rebar in concrete under chloride environment[J]. Corrosion Science, 2015, 93(4):267-282. [5] Zhang Z W, Li Y S, Liu R. Failure behavior of adhesive bonded interface between steel and bamboo plywood[J]. Journal of Adhesion Science and Technology, 2016, 30(19):2081-2099. [6] Zhang J L, Li Y S, Liu R, et al. Examining bonding stress and slippage at steel-bamboo interface[J]. Composite Structures, 2018, 194(15):584-597. [7] Pan C G, Jin W L, Mao J H, et al. Influence of reinforcement mesh configuration for improvement of concrete durability[J]. China Ocean Engineering, 2017, 31(5):631-638. [8] Papadakis V G, Vayenas C G, Fardis M N. Fundamental modeling and experimental investigation of concrete carbonation[J]. ACI Materials Journal, 1991, 88(4):363-373. [9] 徐金霞, 冯伟蒋, 林华, 等. 表面活性剂对水泥浆体结合氯离子性能的影响[J]. 湖南大学学报(自然科学版), 2017, 44(12):74-81. [10] Geng J, Easterbrook D, Li L Y, et al. The stability of bound chlorides in cement paste with sulfate attack[J]. Cement and Concrete Research, 2015, 68:211-222. [11] Angst U, Elsener B, Larsen C K, et al. Critical chloride content in reinforced concrete: A review[J]. Cement and Concrete Research, 2009, 39(12):1122-1138. [12] 蒋林华, 刘蓉, 莫莉莉. 阳离子类型对混凝土中钢筋腐蚀临界氯离子浓度的影响[J]. 江苏大学学报(自然科学版), 2013, 34(4):476-480. [13] 岳青滢, 丁宁, 王石付. 阳离子类型对混凝土固化氯离子能力的影响机理[J]. 混凝土, 2014(1):12-16; 20. [14] 潘从玲, 储洪强, 蒋林华. 氯盐-硫酸盐共存环境中阳离子类型对氯离子结合能力的影响[J]. 混凝土, 2019(4):28-32; 36. [15] 张邦庆, 储洪强, 蒋林华. 电化学脱盐对结合氯离子稳定性的若干影响因素研究[J]. 材料导报, 2015, 29(20):70-75. [16] Pruckner F, Gj?rv O E. Effect of CaCl2 and NaCl additions on concrete corrosivity[J]. Cement and Concrete Research, 2004, 34(7):1209-1217. [17] 谢超, 王起才, 李盛, 等. 养护温度和水灰比对混凝土微观孔结构及抗氯离子渗透性影响研究[J]. 硅酸盐通报, 2015, 34(12):3663-3669. [18] Zhang J L, Li Y S, Tong K T, et al. Deformation of steel-bamboo composite beam considering the effect of interfacial slippage[J]. Advanced Steel Construction, 2018, 14(3):324-336. [19] 勾密峰, 管学茂, 张海波, 等. 钙矾石结合氯离子能力的研究[J]. 材料导报, 2013, 27(10):136-139. |
| 备注/Memo: | 收稿日期: 2019－07－22. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/基金项目: 国家自然科学基金（51778302）.第一作者: 林楠（1995－）, 男, 浙江宁波人, 在读硕士研究生, 主要研究方向: 混凝土结构耐久性. E-mail: 1275310925@qq.com*通信作者: 柳俊哲（1964－）, 男, 黑龙江五常人, 博导/教授, 主要研究方向: 混凝土结构耐久性. E-mail: liujunzhe@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |