改性硫氧镁胶凝材料的配制及性能研究
PDF下载 (725)巴明芳 1,王婕斐 1,杨莹莹 1,赵思敏 1,唐哲宇 1,刘佳彬 2.改性硫氧镁胶凝材料的配制及性能研究[J].宁波大学学报(理工版),2014,27(02):83-87.DOI:
BA Ming-fang 1,WANG Jie-fei 1,YANG Ying-ying 1,ZHAO Si-min 1,TANG Zhe-yu 1,LIU Jia-bin 2.Preparation and Property of Modified Magnesium Oxy-sulfate Materials[J].Journal of Ningbo University(Natural Science & Engineering Edition),2014,27(02):83-87.DOI:
| Title: | Preparation and Property of Modified Magnesium Oxy-sulfate Materials |
| 作者: | 巴明芳 1, 王婕斐 1, 杨莹莹 1, 赵思敏 1, 唐哲宇 1, 刘佳彬 2 |
| Author(s): | BA Ming-fang 1, WANG Jie-fei 1, YANG Ying-ying 1, ZHAO Si-min 1, TANG Zhe-yu 1, LIU Jia-bin 2 |
| 关键词: | 硫氧镁; 胶凝材料; 轻烧氧化镁粉; 七水硫酸镁; MgSO4·7H2O |
| Keywords: | sulfur-oxygen magnesium; cemented materials; lightly calcined magnesia powder |
| 分类号: | TQ52 |
| 文献标识码: | A |
| 摘要: | 为确定工业级轻烧氧化镁粉与七水硫酸镁溶液配制改性硫氧镁胶凝材料的最优参数, 分别研究了不同氧化镁/七水硫酸镁摩尔比, 硫酸镁溶液浓度及水稳剂水玻璃对硫氧镁胶凝材料工作和力学性能的影响. 结果表明: 随着氧化镁/硫酸镁摩尔比的提高, 硫氧镁水泥的初凝时间逐渐缩短, 流动性逐渐降低, 抗压和抗折强度逐渐提高; 随着七水硫酸镁浓度的提高, 硫氧镁水泥的抗压抗折强度也呈现增长趋势, MgO:MgSO4•7H2O:H2O摩尔比为14:1:12时, 硫氧镁胶凝材浆体的28d抗压和抗折强度分别达到38.3MPa和7.0MPa. 耐水性研究表明, 加入氧化镁质量2%的水玻璃可以很好地改善硫氧镁水泥的耐水性. |
| Abstract: | In order to determine the best preparing parameter of the modified sulfur-oxygen magnesium cementitious materials mixed with industrial-grade MgO powder with average particle size of 54.65μm and MgSO4·7H2O solution, the effects of MgO/MgSO4 molar ratio, the concentration level of solution MgSO4·7H2O and water glass on the working and mechanical properties on sulfur-oxygen magnesium cement are investigated. Results show that the initial setting time and workability of sulfur-oxygen magnesium cemented material gradually decreases along with corresponding strength increasing with the rise of MgO/MgSO4 molar ratio; When MgO/MgSO4·7H2O/H2O molar ratio reaches 14:1:12, the working performance and mechanical properties of sulfur-oxygen magnesium cemented material are found to be the best with 38.3MPa 28d compressive strength and 7.0MPa 28d flexural strength. Also found is that the water resistance of sulfur-oxygen magnesium cemented materials can be further improved by adding 2% water glass. |
| 参考文献 /References: | [1] 严育通, 景燕, 马军. 氯氧镁水泥的研究进展[J]. 盐湖研究, 2008, 16(1):61-66. [2] 张勇, 朱永昌, 李俊, 等. 废玻璃改性氯氧镁水泥的研究[J]. 武汉工程大学学报, 2011, 33(10):54-56. [3] 金育辉, 肖力光, 赵彦迪. 外加剂对氯氧镁水泥抗水性能的影响[J]. 吉林建材, 2000, 82(2):11-13. [4] 李早元, 靳东旭, 周超, 等. 镁氧水泥用于油井堵漏及暂闭的室内研究[J]. 西南石油大学学报: 自然科学版, 2011, 33(5):152-156. [5] 余红发. 新型抗水抓氧镁水泥的研究[J]. 硅酸盐学报, 1992, 20(4):374-380. [6] Demediuk T, Cole W F A. Study of magnesium oxy-sulphates[J]. Australian Journal of Chemistry, 1957, 10(2):287-294. [7] Beaudoin J J, Ramachandran V S. Strength development in magnesium oxy-sulfate cement[J]. Cement and Concrete Research, 1978, 8(l):103-112. [8] 朱会荣. 硫氧镁胶凝材料性能的研究[D]. 长春: 吉林建筑工程学院, 2010. [9] 阮炯正, 朱会荣, 梁锐, 等. 硫氧镁胶凝材料性能与研究[J]. 吉林建筑工程学院学报, 2009, 26(4):17-25. [10] 罗建国, 姚吉升, 孙建鄂. MgO-MgSO4-H2O胶凝体系水化动力学的研究[J]. 硅酸盐学报, 1998, 6(2):157- 161. [11] 邓德华. 提高镁质碱式盐水泥性能的理论与应用研究[D]. 长沙: 中南大学, 2005. |
| 备注/Memo: | 收稿日期: 2013-06-05. 宁波大学学报（理工版）网址http://journallg.nbu.edu.cn/ 基金项目: 浙江省大学生科技创新活动计划暨新苗人才计划（2013R405012, 003-21021003）. 第一作者: 巴明芳（1975－）, 女, 山东滨州人, 博士/工程师. 主要研究方向: 高性能绿色建筑材料. E-mail: bamingfang@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |