PDF下载 (45816)赵哲骐 1,2,孙宝寿 1,2*,束学道 1,2,彭文飞 1,2.基于正交试验的高铁轴承内圈冷辗扩壁厚均匀性优化分析[J].宁波大学学报(理工版),2017,30(4):6-10.DOI:
ZHAO Zhe-qi 1,2,SUN Bao-shou 1,2*,SHU Xue-dao 1,2,PENG Wen-fei 1,2.Optimization analysis of wall thickness uniformity of inner ring of high speed rail bearing on cold rolling based on orthogonal test[J].Journal of Ningbo University(Natural Science & Engineering Edition),2017,30(4):6-10.DOI:
| Title: | Optimization analysis of wall thickness uniformity of inner ring of high speed rail bearing on cold rolling based on orthogonal test |
| 作者: | 赵哲骐 1, 2, 孙宝寿 1, 2*, 束学道 1, 2, 彭文飞 1, 2 |
| Author(s): | ZHAO Zhe-qi 1, 2, SUN Bao-shou 1, 2*, SHU Xue-dao 1, 2, PENG Wen-fei 1, 2 |
| 关键词: | 非对称; 壁厚均匀性; 正交试验; 工艺参数 |
| Keywords: | asymmetric; wall thickness uniformity; orthogonal test; process parameter |
| 分类号: | TG335.12 |
| 文献标识码: | A |
| 摘要: | 为提高高铁轴承内圈冷辗扩成形壁厚均匀性, 应用ABAQUS软件建立高铁轴承内圈非对称冷辗扩有限元模型, 并进行了相关模拟. 基于正交试验方法, 以冷辗扩成形后轴承内圈的壁厚均匀性为试验指标, 获得了芯辊初始进给速度(A)、锥辊转速(B)和驱动辊转速(C)对壁厚均匀性的影响规律, 并利用极差分析法和方差分析法对轴承内圈冷辗扩工艺参数进行优化. 研究结果表明, 工艺参数对内圈壁厚均匀性影响的主次顺序为 , 并得到了最佳工艺参数组合. |
| Abstract: | In order to improve the wall thickness uniformity of inner ring of high speed rail bearing on cold rolling, the finite element model of inner ring of high speed rail bearing under asymmetric cold ring rolling process is established through ABAQUS software. Taking the wall thickness uniformity of finished rings as test index, the influence law of the initial feed rate of mandrel (A), cone roller speed (B) and drive roller speed (C) on the wall thickness uniformity is obtained using the orthogonal test method. The parameters of inner ring during cold rolling process are optimized by means of range analysis and variance analysis. The analytical results show that the order of influence of process parameters on the wall thickness uniformity of inner ring is C >A×C >B×C >A >B > A×B, and the optimum combination of process parameters is obtained. |
| 参考文献 /References: | [1] 李春天, 黄欣. 环件轧制技术及其在国内的应用[J]. 锻压装备与制造技术, 2004, 39(5):8-13. [2] 华林, 韩星会. 环件冷轧技术及其在轴承行业中应用[J]. 金属加工: 热加工, 2008(7):17-19. [3] 王令文, 朱蔚. 套圈毛坯的冷辗扩工艺[J]. 轴承, 2002(l):41-43. [4]华林, 左治江, 兰箭, 等. 沟球断面环件冷辗扩三维有限元模拟与工艺设计[J]. 中国机械工程, 2008, 44(10):201-205. [5] 华林, 左治江, 兰箭, 等. 环件冷辗扩芯辊进给速度规范设计[J]. 中国机械工程, 2006, 17(9):953-957. [6] 杨合, 李兰云, 王敏, 等. 异型环件冷辗扩中环件半径扩大变形行为研究[J]. 中国科学: 技术科学, 2010, 40(7):802-810. [7] 靳妍妍, 钱东升, 石磊. L形截面轴承套圈冷辗扩数值模拟与试验[J]. 轴承, 2016(7):15-20. [8] 赵玉民, 彭巍, 杨金娥. 阶梯形轴承内圈冷辗扩成形与模拟研究[J]. 轴承, 2006(8):12-15. [9] 华林, 钱东升. 轴承环轧制成形理论和技术[J]. 机械工程学报, 2014, 50(16):71-75. [10] 魏文婷, 华林, 韩星会, 等. 大变形量下高碳钢环件冷轧变形过程模拟与实验研究[J]. 中国机械工程, 2015, 26(4):540-544. |
| 备注/Memo: | 收稿日期: 2016－10－30. 宁波大学学报（理工版）网址: http://journallg.nbu.edu.cn/ 基金项目: 国家自然科学基金（51475247）; 宁波市重点学科基金项目（XKL14D2048）; 宁波市自然科学基金（2015B11045）. 第一作者: 赵哲骐（1990－）, 男, 浙江宁波人, 在读硕士研究生, 主要研究方向: 塑性成形工艺与装备; E-mail: zhaozheqii@163.com *通信作者: 孙宝寿（1960－）, 男, 江苏泰兴人, 副教授, 主要研究方向: 塑性成形工艺与装备; E-mail: sunbaoshou@nbu.edu.cn 宁波大学学报（理工版）网址：http://journallg.nbu.edu.cn/ |