工艺参数对5CrNiMo18变截面锥形薄壁回转件强力旋压成形壁厚均匀性影响
PDF下载 (491)束学道 1,2,朱 颖 1,2.工艺参数对5CrNiMo18变截面锥形薄壁回转件强力旋压成形壁厚均匀性影响[J].宁波大学学报(理工版),2018,31(1):8-12.DOI:
SHU Xue-dao 1,2,ZHU Ying 1,2.Influence of process parameters on the wall thickness precision by power spinning of thin-walled conical part of 5CrNiMo18 with discontinuous wall thickness[J].Journal of Ningbo University(Natural Science & Engineering Edition),2018,31(1):8-12.DOI:
| Title: | Influence of process parameters on the wall thickness precision by power spinning of thin-walled conical part of 5CrNiMo18 with discontinuous wall thickness |
| 作者: | 束学道 1, 2, 朱 颖 1, 2 |
| Author(s): | SHU Xue-dao 1, 2, ZHU Ying 1, 2 |
| 关键词: | 锥形回转件; 强力旋压; 壁厚均匀性; 变截面 |
| Keywords: | conical part; power spinning; wall thickness deviation; discontinuous wall thickness |
| 分类号: | TG376.2 |
| 文献标识码: | A |
| 摘要: | 锥形薄壁回转件大量应用于航空航天领域, 变截面锥形回转件是其中难以成形的零件之一. 本文基于Simufact.Forming仿真软件, 对5CrNiMo18不锈钢材料强力旋压成变截面锥形薄壁回转件的过程进行仿真模拟, 分析芯模转速、旋轮进给比、摩擦系数3个主要工艺参数对锥形件的壁厚均匀性的影响. 使用正交试验方法设置参数组合, 用极差法分析试验数据, 得出影响因素的主次及较优参数组合. 研究表明: 当芯模转速1200mm·min-1, 旋轮进给比1mm·r-1, 摩擦系数0.15时, 壁厚极差最小. 旋轮进给比对壁厚极差影响最大, 随着旋轮进给比增大, 壁厚极差先增大后减小; 芯模转速对壁厚极差影响次之, 随着芯模转速增大, 壁厚极差先减小后增大. 研究结果为提高旋压成形航空机匣质量提供了理论基础. |
| Abstract: | Conical parts with thin wall have been largely applied in the aerospace fields, and the discontinuous wall thickness conical part is one of them, which is difficult in spinning. Based on the Simufact-Forming software, the finite element model of the conical part with the thin wall of 5CrNiMo18 stainless steel is established. The influence of process parameters, including mandrel rotary velocity, feed rate of roller and friction coefficient between roller and blank, on the wall thickness deviation is analyzed. The process parameters are designed by means of the orthogonal tests, and then the data of the wall thickness deviation is analyzed. The results indicate that the optimum forming quality can be obtained under the mandrel rotary velocity being 1200mm·min-1, the feed rate being 1mm·r-1, and the coefficient of friction being 0.15. It is found that the feed rate is the best impact factor for the thickness reduction ratio as it increases firstly followed by decreasing. Also noted is that the mandrel rotary velocity is influenced by the wall thickness, as the increasing of mandrel rotary velocity, the wall thickness decreases firstly and then increases. The findings set up a theoretical basis for the spinning of case that is applicable in aerospace industry. |
| 参考文献 /References: | [1] 夏琴香, 周立奎, 肖刚锋, 等. 工艺参数对高强钢锥形件剪切旋压成形质量的影响[J]. 锻压技术, 2017, 42(2):77-81. [2] 王雨, 束学道, 田端阳, 等. 工艺参数对薄壁锥形旋压件凸缘平直度的影响[J]. 机械科学与技术, 2017, 36(7):1068-1072. [3] 周强. 突变壁厚锥形件强力旋压成形有限元模拟和试验研究[D]. 西安: 西北工业大学, 2007. [4] 徐银丽, 詹梅, 杨合, 等. 锥形件变薄旋压回弹的三维有限元分析[J]. 材料科学与工艺, 2008, 16(2):167-171. [5] Chen M D, Hsu R Q, Fuh K H. Forecast of shear spinning force and surface roughness of spun cones by employing regression analysis[J]. International Journal of Machine Tools and Manufacture, 2001, 41(12):1721-1734. [6] 刘伟军, 吴耀金, 薛勇, 等. AZ80镁合金锥形件内环筋挤压成形工艺参数研究[J]. 热加工工艺, 2015, 44(3):119-122. [7] Kalpakcioglu S. An experimental study of plastic deformation in power spinning[J]. CIRP Annals, 1961, 1:58. [8] 位杰, 束学道, 何杰. 工艺参数对高铁轴承外圈端面成形质量的影响[J]. 宁波大学学报(理工版), 2016, 29(3):103-106. [9] 束学道, 田端阳, 王雨, 等. 浮压法压实斜轧钢球内部空洞的条件[J]. 宁波大学学报(理工版), 2017, 30(1):1-6. [10] 王岩, 隋思涟. 试验设计与MATLAB数据分析[M]. 2版. 北京: 清华大学出版社, 2013:65-88. [11] 日本塑性加工学会. 旋压成形技术[M]. 北京: 机械工业出版社, 1988:144-146. [12] 王成和, 刘克璋, 周路. 旋压技术[M]. 福州: 福建科学技术出版社, 2017:710-721. |