带肋钢筋套筒灌浆连接破坏过程的有限元分析
PDF下载 (167)郎圣淳,严晓东.带肋钢筋套筒灌浆连接破坏过程的有限元分析[J].宁波大学学报(理工版),2025,38(1):37-44.DOI:10.20098/j.cnki.1001-5132.2023.1112
LANG Shengchun,YAN Xiaodong.Finite element analysis of damage process of grouted sleeve connections with ribbed reinforcing bars[J].Journal of Ningbo University(Natural Science & Engineering Edition),2025,38(1):37-44.DOI:10.20098/j.cnki.1001-5132.2023.1112
| Title: | Finite element analysis of damage process of grouted sleeve connections with ribbed reinforcing bars |
| 作者: | 郎圣淳, 严晓东 |
| Author(s): | LANG Shengchun, YAN Xiaodong |
| 关键词: | 有限元分析; 套筒灌浆连接; 破坏模式; 裂缝开展; 黏结强度 |
| Keywords: | finite element analysis; grouted sleeve connection; damage mode; crack development; bond strength |
| 分类号: | TU375 |
| DOI: | 10.20098/j.cnki.1001-5132.2023.1112 |
| 文献标识码: | A |
| 摘要: | 为揭示套筒灌浆连接接头的细观工作机理, 采用ABAQUS软件建立接头三维精细化有限元模型, 模拟接头内部灌浆料的开裂和破坏过程, 分析造成不同破坏模式的主要原因. 结果表明, 钢筋锚固区灌浆料的裂缝呈现45°夹角分布, 在套筒端发生较为严重的楔形破坏, 纯灌浆段有水平贯穿裂缝; 增大钢筋锚固长度能够减小纯灌浆段水平贯穿裂缝的数量; 钢筋肋间灌浆料的受压情况决定套筒灌浆接头最终的破坏模式; 利用新模型能够准确反映接头的破坏模式和荷载—位移曲线. |
| Abstract: | In order to reveal the fine working mechanism of the grouted sleeve connections, a three-dimensional refined finite element model was established in ABAQUS to analyze the cracking and destruction process of the grout, and to study the main reasons for the different destruction modes. The results show that the cracks in the grouting material at the steel bar anchorage zone exhibited a 45° angle distribution, and severe wedge-shaped damage occurred at the sleeve end. There were horizontal penetrating cracks in the pure grouting section, and their number can be reduced by increasing the anchorage length of steel bars. The compression condition of the grouting material between the steel bars determines the final failure mode of the grouted sleeve connections. The presented model can accurately demonstrate the damage mode and load displacement curve of the grouted sleeve connections. |
| 参考文献 /References: | [1].张丽华, 刘洋, 刘敏敏, 等. 钢筋套筒灌浆接头抗拉性能影响因素试验研究[J]. 安全与环境学报, 2020, 20(2): 463-472. [2].刘良林, 肖建庄. 钢筋套筒灌浆连接研究进展[J]. 建筑结构学报, 2023, 44(1):235-247. [3].苗吉军, 刘远霖, 刘才玮, 等. 灌浆套筒力学性能影响因素研究进展[J]. 科学技术与工程, 2023, 23(3):905- 918. [4].ZHENG G Y, KUANG Z P, XIAO J Z, et al. Mechanical performance for defective and repaired grouted sleeve connections under uniaxial and cyclic loadings[J]. Construction and Building Materials, 2020, 233:117233. [5].YANG C, ZHANG L Y M, ZHANG Z Y, et al. Effective stress-strain relationship for grouted sleeve connection: modeling and experimental verification[J]. Engineering Structures, 2020, 210:110300. [6].刘良林, 肖建庄, 丁陶. 套筒灌浆连接受力失效机理与有限元仿真验证[J]. 工程力学, 2022, 39(12):177-189. [7].鲍佳文. 新型灌浆套筒连接性能和粘结滑移关系的精细有限元分析[D]. 杭州: 浙江大学, 2022. [8].鲍佳文, 高强, 唐林, 等. 钢筋套筒灌浆连接拉伸性能的精细有限元分析[J]. 浙江大学学报(工学版), 2023, 57(4):814-823. [9].罗小勇, 龙昊, 曹琨鹏. 灌浆套筒连接装配式梁柱节点精细有限元模型[J]. 哈尔滨工程大学学报, 2021, 42(5): 641-648. [10].王宁, 车文鹏, 武立伟, 等. 新型12mm钢筋灌浆套筒连接力学性能试验研究及有限元分析[J]. 工业建筑, 2019, 49(4):81-87, 94. [11].WU M, LIU X, LIU H T, et al. Seismic performance of precast short-leg shear wall using a grouting sleeve connection[J]. Engineering Structures, 2020, 208:110338. [12].刘良林, 肖建庄, 李建新, 等. 高温后灌浆料静动态单轴受压力学性能[J]. 工程科学与技术, 2022, 54(4):112- 120. [13].鲍佳文, 赵唯坚, 高强, 等. 套筒灌浆接头黏结滑移关系的精细有限元分析[J]. 哈尔滨工业大学学报, 2024, 56(2):68-76. [14].WU M, LIU H, DU X. Effect of tapered head sleeve structural parameters on grouting connection joints deformation[J]. Journal of Materials in Civil Engineering, 2020, 32(5):04020083. [15].唐林. 单向拉伸荷载下新型套筒灌浆连接长度试验研究[D]. 沈阳: 沈阳建筑大学, 2017. [16].王腾辉, 陈权, 夏文传, 等. 基于ABAQUS塑性损伤的半灌浆套筒力学性能有限元分析[J]. 科学技术与工程, 2022, 22(9):3709-3715. [17].YUN X, GARDNER L. Stress-strain curves for hot-rolled steels[J]. Journal of Constructional Steel Research, 2017, 133:36-46. [18].FU T, HOU J P, ZHU Z X, et al. Experimental study on UHPC-based grouting materials and mechanical performance of grouted splice sleeve joints[J]. Frontiers in Materials, 2022, 9:912509. [19].XU F, WANG K, WANG S G, et al. Experimental bond behavior of deformed rebars in half-grouted sleeve connections with insufficient grouting defect[J]. Construction and Building Materials, 2018, 185:264-274. |